Prevention of molecular weight reduction of the polymer, impurity formation and gelling in polymer compositions

ABSTRACT

Polymer and drug containing compositions and method of preparing such compositions are disclosed. The dispersed phase formulation has a polymer, a pharmaceutically or biologically active agent and a small fraction of low pKa acid additive. Stable, filter sterilizable, non-gelling solutions containing GnRH analogues at least at levels typically used in sustained release formulations and a method of increasing solubility of a high level of a GnRH analogue or a freeze-dried antgonist of GnRH in a polymer containing solution are also disclosed. The amount of the acid additive in the polymer solution is such that it is sufficient to increase the solubility of the high level of the GnRH analogue in the polymer solution without affecting the release characteristics of the microspheres prepared therefrom.

This application claims the benefit of U.S. Provisional Application No. 60/488,573 filed Jul. 18, 2003, and the text of application 60/488,573 is incorporated by reference in its entirety herewith.

FIELD OF THE INVENTION

The present invention relates to polymer compositions capable of providing sustained or extended drug release, methods of their preparation and use in various biological applications. Specifically, it relates to prevention or elimination of molecular weight reduction of the polymer in a polymer solution containing nucleophilic compound(s) or agent(s). It also relates to reduction or elimination of peptide polymer impurities in the polymer solutions. It further relates to GnRH analog and polymer containing solutions capable of forming stable, filter sterilizable, non-gelling solutions.

BACKGROUND OF THE INVENTION

Compositions containing biologically active agents in combination with biocompatible and biodegradable polymers are being increasingly used as drug delivery systems to provide sustained or delayed release of drugs. The compositions are available in various injectible depot forms including liquid forms, solid implants, microspheres, microcapsules and microparticles.

For example controlled release systems where the polymeric compositions are liquid forms or flowable delivery sytems are described in U.S. Pat. Nos. 5,739,176, 4,938,763; 5,278,201, 5,324,519 and 5,278,202. The compositions described in these patents are administered to the body of a subject in a flowable state. Once in the body, the composition precipitates or coagulates to form a solid matrix or implant and the organic solvent in the composition dissipates or disperses into the aqueous or body fluid. Once the solid implant is formed, usually at the site of administration, the biologically active agent is released from the solid matrix by diffusion or dissolution from within the polymeric matrix and/or by the slow degradation of the polymeric matrix.

A variety of sustained release microspheres or microcapsules are also available or are being developed as delivery systems for the rapidly expanding class of peptide and non-peptide therapeutic or pharmacological agents. For example, sustained release microspheres or microcapsules are known in the administration of hormones, hormone analogs, antitumoral drugs, thioridazine, antipsychotic, and steroids where PLGA o PLA is the constitutive biodegradable polymer material. Further, for example, in recent years, a variety of injectable depot formulations in which a somatostatin analog (e.g., octreotide acetate) or a LHRH analog (e.g. leuprolide acetate) encapsulated in, and released slowly from, microspheres made of biodegradable polymers have been reported (U.S. Pat. Nos. 5,478,564, 5,540,973, 5,609,886, 5,876,761, 5,688,530, 4,652,441, 4,677,191, 4,917,893, 4,954,298, 5,330,767, 5,476,663, 5,575,987, 5,631,020, 5,631,021 and 5,716,640). Indeed, long acting injectable depot formulations of GnRH analogues (agonists and antagonists) are being used and/or tested for the treatment of various pathological and physiological conditions in mammals, particularly in humans (Kostanski et al., 2001, BMC Cancer, 1:18-24). The treatments are for, among other things, the management of sex hormone-dependent diseases such as prostate cancer and endometriosis, for the induction of ovulation, and for the control of male fertility.

Thus, significant efforts are being made to maintain a steady release of medicinal drugs in animals by using compositions containing biodegradable biocompatible polymers. One obvious goal behind in all of these polymeric compositions is that the biologically active agent (e.g., a peptide or protein) of interest can be administered less frequently, sometimes at lower overall doses, than when formulated as a solution without the use of polymers in them. More importantly, it can justify commercial development of proteins that, for a variety of reasons, could not be marketed as simple solution formulations.

Despite the technological advances that were made in the area of injectable depot formulations to date, a number of quality concerns prevent their ready use in biological applications. These include reduction in molecular weight of the polymers in the polymer composition, de novo formation of conjugate substances (impurities), insolubility of the biologically active agents in solvents typically used in the polymer compositions and their propensity to form gels.

Molecular weight of the polymer material (e.g., PLGA/PLA matrix) is an important factor in designing sustained release formulations because drug release profile and the degradation rate of the polymer depend on molecular weight of the polymer in the final product. It has been reported that the molecular weight of the PLGA decreased in the microcapsules (microspheres) containing simple basic compounds such as thioridazine and ketotifen as free bases during their fabrication. Microcapsules fabricated from their pamoate salts did not produce much reduction in molecular weight (Maulding et al., 1986, Journal of Contolled Release, 3:103-117). U.S. Pat. No. 5,916,598 showed that the presence of benzyl alcohol, as the residual solvent in the microspheres reduced the shelf life of the product by molecular weight reduction and the patent provides a method to reduce the residual benzyl alcohol level. However, it is not always possible to remove the residual solvents from the microspheres.

U.S. Pat. No. 6,264,987 discloses that the simple nucleophilic compounds such as risperidone, naltrexone, and oxybutynin can degrade the PLGA variably depending upon the holding time and temperature of the dispersed phase solution. Methods provided to minimize the reduction in molecular weight are, lowering the hold time of the drug-polymer solution and the hold temperature. However, during the manufacturing of the sustained release products, it is very difficult to control the hold time of the drug-polymer solutions. Also, the hold time and its effect may depend upon the type, co-monomer ratio and co-monomer sequence of the polymer. Further, there could be unexpected delays in the aseptic processing sequence during the fabrication of microspheres, which could make the entire drug-polymer solution not usable. Lowering the hold temperature of the drug-polymer solution could result in drug crystallization or viscous polymer-drug solution. Higher viscosity solutions are difficult to sterile filter and often give rise to larger particles. Larger particles could pose syringeability problems.

The FDA and ICH guidelines on impurities in new drug substances suggest that any impurity (individual impurity) greater than 0.1% has to be reported, and any impurity greater than 0.15% has to be identified. If the impurity in a new drug is more than a given threshold level, those impurities should be adequately tested for their adverse effects and biological safety. It is generally understood that there is no safety concern if the individual impurity is less than 0.5% or the total impurity, which is the sum of individual impurities, is less than 2% in, for example, a peptide containing polymer composition. These levels define threshold levels. Thus, the use of peptide or protein drug-containing polymer composition with individual impurity greater than 0.5% and/or total impurity greater than 2% may raise regulatory compliance issues. Often, peptide related substances or impurities in microsphere formulations, manufactured by the currently known processes, exceed levels far greater than the threshold levels. The extent of impurity depends upon the type of peptide. Decreasing the level of impurity to not more than the threshold can be simpler and economical than providing safety data.

Most of the GnRH analogues, particularly antagonists, are not freely soluble in water or in other solvents and they have a propensity to form gels even at low concentrations (Ref: J. Med. Chem., 2001, 44, 453-467). Sustained release formulations usually require very high concentrations of the analogues dissolved in small volumes water or some other suitable solvent(s). The relatively low solubility of the GnRH analogues and their concentration-dependent propensity to form gels in aqueous or other solvents greatly limit their use in sustained release formulations. Further, in order to prepare sterile sustained release formulations, it is desirable and to filter sterilize the solution of the drug and the polymer matrix (either separately or as a combined solution) rather than resort to sterilization techniques such as heat, steam, gamma radiation and the like.

Therefore, a need exists in the prior art to develop polymer drug compositions and methods thereof that do not raise quality concerns associated with molecular weight reduction of the polymers in the polymer composition, impurities, and solubility and gelling of the biologically active agents used in the compositions.

SUMMARY OF THE INVENTION

It has now been found that it is possible to obtain polymer compositions that address the above discussed quality concerns posed by the prior art compositions.

Specifically, it is now possible to reduce or eliminate the molecular weight reduction of a polymer, which is caused by nucleophilic substance capable of catalyzing ester bond cleavage of the polymer in the polymer composition, by including a small amount of an acid additive as part of the polymer composition. Particularly, if a small amount low pKa acids such as lactic acid, glycolic acid or oligomer acids are incorporated into the polymer-drug solution, it can considerably reduce or eliminate the molecular weight reduction of the polymer.

It is also now made possible to minimize or eliminate peptide polymer conjugates (impurities) in polymer compositions by carrying out certain manipulations during the polymer composition preparation process i.e., by selecting a right polymer having an acid number of between 10 and 40 or a right molar ratio of different monomers in a copolymer and/or by adding one or more low pKa acids to the polymer composition.

It has also been found in the present invention that one can obtain stable solutions containing GnRH analogues at least at levels typically used in polymer compositions without the associated solubility and/or gelling problems by using a freeze-dried GnRH analogue and at least one solvent in which the GnRH analogue dissolves as components of the polymer composition.

Accordingly, in one aspect relating to the molecular weight reduction of the polymer, the present invention discloses polymer compositions and methods for preparing such compositions. In an embodiment, the composition has a biocompatible and biodegradable polymer (e.g., poly(d,l-lactic acid), poly(l-lactic acid), poly(glycolic acid) or copolymers of these monomers), at least one nucleophilic ingredient capable of cleaving ester bonds of the polymer and causing molecular weight reduction of the polymer, and a low amount of an acid additive. The nucleophilic substance may be a solvent (e.g., methanol, propanol, isopropanol, tert-butanol or benzyl alcohol) or a compound such as a peptide, ketotifen, thioridazine, olanzapine, risperidone, oxybutynin, naltrexone, octreotide, leuprolide, orntide or Woc4D or pharmaceutically acceptable salts thereof. The acid additive can be lactic acid, glycolic acid, acetic acid, glyceric acid, benzoic acid, propanoic acid or carboxy terminated oligomers of lactic acid, carboxy terminated oligomers of glycolic acid, individually or a combination of these acids. It can be used in an amount of about 0.1% to about 50% relative to the amount of the polymer in the composition. Due to the presence of such an acid additive in the polymer composition, the polymer in the composition is less susceptible to molecular weight reduction as compared to the composition without the acid additive.

In another aspect, the present invention provides a composition for a dispersed phase formulation having a GnRH analog, and an acid additive so that the GnRH analog remains in soluble form and/or is resistant to gelling. A method of increasing the solubility of a high level of a GnRH analogue in a polymer containing dispersed phase is also provided. It involves dispensing a high level of the GnRH analogue, adding a first organic solvent to the GnRH analogue to form a first organic mixture, dissolving an amount of a polymer in a second organic solvent to form a second organic mixture, mixing the first and second organic mixtures to form the dispersed phase, and adding an amount of an acid additive to the dispersed phase. The amount of the acid additive in the dispersed phase should be sufficient to increase the solubility of the high level of the GnRH analogue in the dispersed phase without affecting the solute release characteristics of any solute bearing microspheres prepared from the dispersed phase.

In yet another aspect, the present invention also provides methods for suppressing the secretion of gonadotropins or steroids in a mammal by administering an effective amount polymer composition of a GnRH analogue that is made more soluble and/or resistant to gelling according to the present invention together with a pharmaceutically acceptable carrier and/or diluent. It includes methods for treatment of hormone related or steroid-dependent pathologies. The polymer compositions of the present invention can be administered to mammals subcutaneously, intramuscularly, intravenously, intranasally, intravaginally or intrarectally to achieve the desired effects such as applications calling for reversible suppression of gonadal activity, in particular reversible suppression of testosterones. Effective dosages can vary with the form of administration and the particular species of mammal being treated.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a histogram showing molecular weight reduction of PLGA in blank and Leuprolide containing DP stored at 25 C for 24 hours.

FIG. 2 is a histogram showing molecular weight reduction of PLGA in blank and Leuprolide containing DP Stored at 40 C for 24 hours.

FIG. 3 is a histogram showing molecular weight reduction of PLGA in blank and Octreotide containing DP stored at 25 C for 24 Hours.

FIG. 4 is a histogram showing molecular weight reduction of PLGA in blank and Octreotide containing DP stored at 40 C for 24 Hours.

FIG. 5 shows relationship between the reduction in molecular weight and related substance formation in leuprolide DP.

FIG. 6 shows relationship between the reduction in molecular weight and related substance formation in Octreotide DP.

FIG. 7 shows HPLC Chromatogram of Octreotide Extract with Peak Identity.

FIG. 8 is a graph showing the effect of molecular weight of the polymer on the level of the related substances.

FIG. 9 is a graph showing the effect of the target load on the amount of related substances formed.

FIG. 10 is a graph showing the effect of percentage glycolide in the polymer on related substance formation.

FIG. 11 is a graph showing relationship between the acid number and the percentage of impurities for the microspheres prepared from PLGA50:50 having a target load 10-12% (FIG. 11A) and from other polymers having a target load 10-13% (FIG. 11B).

FIG. 12 is a histogram showing the effect of acid additives in the dispersed phase on related substance formation.

FIGS. 13A-C are graphs showing related substance formation during in vitro release of peptide drugs from microspheres.

FIG. 14 shows the serum octreotide level in rats injected with octreotide microspheres (microsphere lots GC091903, GC091203, GC091503, GC091703 and GC091603) containing no detectable impurities.

FIG. 15 shows the percentage increase in body weight compared to the time when they received the octreotide microspheres (microsphere lots GC091203, GC091503, GC091603, GC091703 and GC091903) containing no detectable impurities. Control indicates body of weight of rats that received only the diluent.

FIG. 16 is the HPLC chromatogram of the extract from a RG503H microsphere, TV061297.

FIG. 17 shows the serum leuprolide and testosterone levels in prostate cancer patients administered with leuprolide microspheres made according to an embodiment of the invention. The molecular weight of the polymer in these leuprolide microspheres (Mw 14420) remained nearly the same as the molecular weight (Mw 14321) of the raw polymer used for the microsphere preparation.

FIG. 18 is a graph illustrating the effect of an orntide microsphere, GJ082100 prepared in accordance with the present invention, on testosterone suppression in a rat model.

FIG. 19 is a graph illustrating the effect of another orntide microsphere, GJ082400 prepared in accordance with the present invention, on testosterone suppression in a rat model.

FIG. 20 shows serum orntide and serum testosterone levels in rats that received orntide microspheres made of 85:15 PLGA (Mw 81 kDa; referred to herein as GC102301) at 27 mg/Kg body weight.

FIG. 21 shows serum orntide and serum testosterone levels in rats that received orntide microspheres made of PLA (Mw 30 kDa; referred to herein as GC010402) at 27 mg/Kg body weight.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention relates to polymer and drug containing compositions and methods for preparing such compositions for use in providing a steady release of drugs over extended periods (sustained release) in animals including humans. The present invention discloses how to eliminate or lower the reduction of molecular weight of a polymer (e.g., PLGA or PLA) in the polymer composition, how to eliminate or reduce the formation peptide polymer conjugates in the polymer compositions and how to obtain stable solutions containing GnRH analogues at least at levels typically used in sustained release formulations without the associated solubility and/or gelling problems.

The polymer compositions can be in the form of polymer solutions (also referred to herein as dispersed phase or dispersed phase formulations). The polymer solutions or dispersed phase formulations of the present invention necessarily contain, among other things, a polymer and one or more types of peptides or nucleophilic compounds (e.g., a pharmaceutical agent or drug) and at least one solvent (e.g., methanol, propanol, isopropanol, tert-butanol, benzyl alcohol, dichloromethane and dimethylsulfoxide) in them.

The polymer compositions can be in one or more of other sustained release forms such as implants or microspheres or microparticles or such others resulting from processing of the polymer solutions, described above, by using techniques known to those skilled in the art. These techniques include, but not limited to, spray-drying, vacuum-drying, formation of emulsion and solvent evaporation or solvent extraction and spray-freezing. Thus, despite the use of the phrase “dispersed phase” throughout the description herein, the suitability of the polymer solutions is not in any way limited only to dispersal in another phase.

A polymer added to the polymer composition of the present invention can be any polymer that is generally used in preparing polymer compositions or sustained release formulations, and also retains desired characteristics such as desired level biodegradability, permits higher drug load, and in the case of microspheres made from emulsions, enhances solvent removal from the dispersed phase or inhibit drug migration from the dispersed phase into the continuous phase. A number of such polymers are known to those of ordinary skill in the art. See, for example, U.S. Pat. Nos. 5,945,126, 5,407,609, 4,818,542, 4,767,628, 3,773,919 and 3,755,558, the contents of which are incorporated herein by reference. In selecting a particularly desirable polymer for a given system, numerous factors can be considered for purposes of producing a product having the desired clinical characteristics such as biodegradability (e.g., release profile) and biocompatibility.

The polymer is preferably biodegradable and biocompatible. Preferred examples of polymer matrix materials include poly(glycolic acid), poly(d,l-lactic acid), poly(l-lactic acid), copolymers of the foregoing, and the like. Other polymers or other compounds that can be used as matrix materials are polycaprolactone, copolymer of caprolactone with lactide and glycolide, copolymer of lactide and glycolide with polyethylene glycol (called PLGA-PEG or PLA-PEG), and also polyanhydride. Various commercially available poly (lactide-co-glycolide) materials (PLGA) or poly(d,l-lactic) acid (PLA) can be used in the microspheres of the present invention. For example, poly (d,l-lactic-co-glycolic acid) is commercially available from Boehringer Ingelheim, Germany, Alkermes, Inc, Cincinnati, Ohio Birmingham Polymers Inc., Birmingham, Ala. These copolymers are available in a wide range of molecular weights and ratios of lactic acid to glycolic acid. When the copolymer poly(d,l-lactide-co-glycolide) is used, it is preferred to have selected molar ratios of lactide to glycolide in such a copolymer such that it has only 25% or less of glycolide content, though other molar ratios can also be used by practicing the present invention.

The nucleophilic compounds, in the context of the present invention, are those compounds that are capable of cleaving ester bonds (nucleophilic attack) in the polymer or causing the polymer hydrolysis as a result of the nucleophilic attack. The ester bond cleavage obviously results in polymer fragmentation and hence molecular weight reduction of the polymer starting material in the dispersed phase formulation. By practicing the present invention, it is now possible to reduce the molecular weight reduction of the polymer despite the presence of nucleophilic compounds in the dispersed phase formulation.

Regardless of the polymer used, presence of nucleophilic compounds in the dispersed phase do cause molecular weight reduction absent measures taken to prevent such reduction. It is believed that the nuclephilic group (group bearing lone pair of electron) attacks the ester bond of the polymer. The nucleophilic attack can be caused by groups containing replaceable hydrogen atoms (particularly —SH, —NH2, ═NH, —OH) and those that do not contain replaceable hydrogen atoms (e.g., tertiary amine). Examples of nucleophilic compounds or agents that catalyze hydrolysis of the polymer in the dispersed phase include, but are not limited to, methanol, ethanol, propanol, triethylamine, ketotifen, thioridazine, risperidone, olanzapine, oxybutynin or naltrexone or a nucleophilic peptide or pharmaceutically acceptable salts thereof. The peptide can be, for example, octreotide, leuprolide, orntide and Woc4D or a salt thereof.

Most of the polypeptide based drugs contain nucleophilic groups (—SH, —NH2, ═NH, ═N—, or OH) and at least certain amino acids in the peptide drugs are effective nucleophiles toward an ester group of the polymer. Lysine in a peptide, for example, is highly nucleophilic due to primary amine. Examples of the other nucleophiles are arginine, histidine, cystine (provided the —SH group is free and not formed an SS— bond), serine or an amino acid of the peptide having a free amino group.

In general, most of the polypeptide drugs are available as their salts (mostly as acetate salts). For example, leuprolide, orntide and octreotide are available as acetate salts. Even though, the acetate molecule is believed to form an ion pair with the amino groups of the polypeptide it has been found by the present inventors that the nucleophilic groups, even as the acetate salt form, catalyze the polymer (e.g., PLGA) degradation. Further, there are a number of other nucleophilic compounds that are known to one skilled in the art. Therefore, the present invention is not limited to any particular nucleophilic compound specifically described herein and the present invention encompasses such other nucleophilic compounds known in the art or readily apparent to one skilled in the art having the benefit of the present disclosure.

Mostly, presence of nucleophilic peptide compounds in the dispersed phase also leads to the formation of peptide polymer conjugates. Accordingly, there are two issues associated with the nucleophilic attack of peptides on polymer in the polymer solution; polymer molecular weight reduction and adduct formation. Molecular weight of the polymer matrix and drug encapsulation (drug load) are two major factors affecting the release performance of the product. Purity of the drug is another critical parameter for the quality of the product. Hence, it is necessary to control the molecular weight reduction to the extent possible to produce microspheres with very low impurity level.

It has now been found that adding a small amount of an acid additive to the dispersed phase formulation can at least partially protect the polymer in the dispersed phase formulation from the nucleophilic attack thereby controlling the undesirable molecular weight reduction. Specifically, a low pKa acid in small amount can lower the molecular weight reduction of polymer (e.g., poly-D,L-lactide-co-glycolide also referred to herein as PLGA or poly-D,L-lactide also referred to herein as PLA) induced by such nucleophilic attacks. Low pKa acids, as used in the context of the present invention, are those that have a pKa value of 5.0 or lower. Preferred low pKa acids, for example, are propoanoic acid (pKa=4.86), glacial acetic acid (pKa=4.76), benzoic acid (pKa=4.19) or derivatives thereof, glycolic acid (pKa=3.83), glyceric acid (pKa=3.25), lactic acid (pKa=3.08), carboxy terminated oligomers of lactic acid, glycolic acid or the combination of these acids at any ratio having molecular weight not greater than 1000. Particularly preferred acids for preventing the molecular weight reduction of the polymer are glycolic acid, lactic acid and oligomer acids.

It has also been found in the present invention that the acid additive in the dispersed phase reduced or eliminated formation of conjugates between the peptide and the fragments of the polymer, which conjugates (also referred to herein as peptide related substances) are considered to be impurities for clinical purposes and hence are undesirable.

The amount of acid additive in the dispersed phase is such that it is sufficient to confer its protective role against nucleophilic attack on the polymer in the dispersed phase. The amount of acid in the polymer solution can be 5% or higher. The preferred amounts of acid additive may range from about 0.1% to about 5% in the dispersed phase. The particularly preferred amounts of acid additive are from about 1.0% to about 10% in the dispersed phase.

Alternatively, the amount of acid additive to be added to the dispersed phase can also be determined based on the amount of a nucleophilic agent or in terms of the amount of polymer in the dispersed phase, i.e., in terms of parts by weight of the acid additive per total weight of the polymer or % of acid additive per % of polymer in the dispersed phase. If based on the amount and composition of nucleophilic agent such as a solvent, for example, methanol, the amount of acid can be equal to that of the solvent nucleophilic agent. This way, the methanol or other nucleophilic agent induced MW reduction can be significantly reduced or eliminated. The amount of acid can be in stochiometric equivalent of the nucleophilic groups in the DP. In one embodiment, the amount of acid is as low as about 0.01% or 2% and as high as about 50% by weight of the polymer. Preferably the % of acid, relative to or based on the polymer in the dispersed phase is from about 2.0% to about 20%. If the acid additive being used is for the purpose of reducing molecular weight reduction of the polymer, the amount of acid may not be 100% relative to the amount of the polymer in the dispersed phase. If the acid additive being used is for the purpose of preventing gelling (discussed further herein) higher amounts of acid may be used. For example, the amount of acid may be 100% relative to the amount of the polymer in the dispersed phase. In some instances it can even exceed the amount of the polymer.

The acid additive may consist of only one low pKa acid or more than one such acid. The acid additive to be added to the dispersed phase formulation can be either in a solution form or a non-solution form such as, fine dispersion.

In an embodiment of the present invention, a dispersed phase for fabricating microspheres is prepared as follows: a nucleophilic compound (e.g. a polypeptide or protein based drug containing nucleophilic group(s)) and an amount of an acid additive are mixed as such, or these two dissolved or dispersed in a suitable organic solvent (e.g., methanol or DMSO) to form an organic solution or suspension. Separately an amount of a polymer material (e.g., PLGA) is dissolved in a suitable organic solvent (dichloromethane or DCM) to form a polymer solution. The nucleophilic compound and/or agent containing solution or suspension and the polymer solution are mixed to form the dispersed phase. Suitable solvents for preparing polymer containing dispersed phase are known in the art. See, for example, U.S. Pat. No. 5,945,126. Formation of the drug solution or suspension and polymer solution separately could reduce the dissolution time involved in making the dispersed phase. However, the drug and polymer solution could be formed by dissolving them together.

It should be noted that the dispersed phase may contain more than one nucleophilic compound or agent. For example, in the case of a dispersed phase containing octreotide dissolved in methanol, both octreotide and methanol can cleave ester bonds of the polymer in the dispersed phase. In such cases the molecular weight reduction of the polymer in the dispersed phase can be more severe than the dispersed phase containing only one nucleophilic compound. On the other hand, the dispersed phase containing octreotide dissolved in DMSO, only octreotide can cause ester bond cleavage of the polymer in the dispersed phase and, therefore, the molecular weight reduction of the polymer in the dispersed phase is less severe than the dispersed phase containing more than one nucleophilic compound.

Although methanol induced molecular weight reduction can be controlled to a significant extent by adding a low pKa acid to the dispersed phase formulation, higher amount of methanol in the dispersed phase may require higher amount of low pKa acid. Too much acid (>50% in DP) could make the dispersed phase less susceptible for droplet formation in an aqueous continuous phase to form microsphere. However, there will not be any problem in forming microspheres by O/O process. Even to form microspheres by O/W process, compromise amount (ratio) of methanol and low pKa acid could be used in the DP which considerably reduce the MW reduction of the PLGA, and also does not affect disperse phase droplet formation in an aqueous continuous phase. If higher amount of strong acids are desired in the dispersed to minimize the molecular weight reduction and/or related substance formation, alternative solvents such as DMSO and dimethylacetamide (DMAc) can be used. Both DMSO and DMAc are biocompatible solvents. These solvents are miscible with DCM. These solvents can be easily extracted into the continuous phase while preparing the microspheres. Most peptide based drugs are highly soluble in these solvents. A dispersed phase containing DMSO and DMAc can accept higher amount of strong acids without any phase incompatibility problem.

But once microspheres are formed using the dispersed phase formulation, MW reduction of the polymer is not usually seen. It can be determined by testing release profile. The present inventors prepared leuprolide containing microspheres and found the same release profile from the microspheres after 6 month storage at 40° C., two year storage at 25° C.

In an embodiment of the present invention, the preferred drugs may be peptide or protein drugs, steroidal drugs, non-steroidal drugs, and other pharmaceutically active compounds. These include somatostatin analogs, octreotide, lanreotide (LANREOTIDE™), Vapreotide, Woc-2A, Woc-2B, Woc-3A, Woc-3B, Woc-4, Woc-4D and Woc-8 and their salts, compounds with LHRH activity, LHRH analogs, orntide, leuprolide, a thyroid stimulating hormone (TSH), a luteinizing hormone (LH), a follicle stimulating hormone (FSH) and their derivatives, growth factors such as growth hormone releasing peptide (GHRP-1), GH-RH, calcitonin, tumor necrosis factor (TNF), interferon, erythropoietin and others. The preferred drugs are peptide drugs including a lanreotide octreotide, leuprolide, orntide, Woc4D.

Microencapsulation of peptides into biodegradable and non-biodegradable polymers typically involves the formation of a dispersed phase (polymer solution). The dispersed phase includes the peptide of interest, the polymer(s), and the solvents for the drug and the polymer. If the solvent for the polymer and the solvent for the drug are not miscible, the dispersed phase will be an emulsion. For peptide drugs, often the dispersed phase is a water-in-oil emulsion (W/O). It is not necessary that the drug need to be dissolved in a solvent, and the drug could be simply dispersed uniformly as a solid suspension in a polymer solution (S/O system). With appropriate solvent or solvent mixture, it is possible to make the dispersed phase as homogeneous solution (O) for peptide drugs. Emulsification of the dispersed phase into a continuous phase, and the removal of solvent from the dispersed phase results in microsphere/microcapsule formation. The continuous phase could be an aqueous solution, or it could be another oil phase immiscible with the dispersed phase. Thus, the microspheres/microcapsules (which are substantially spherical polymeric particles containing biologically active agents) can be formed by W/O/W, S/O/W, O/W, W/O/O, S/O/O, or O/O system (details of the microsphere/microcapsule preparation can be found in “Handbook of Pharmaceutical Controlled Release Technology, Donald L. Wise (ed.), Mercel Dekker, 2000, Chapter-16, Microsphere Preparation by Solvent Evaporation Method, by A. Atila Hincal and Sema Calis, Pages 329-343”).

In a preferred embodiment, the peptide drug or other active agent is part of a dispersed phase and microspheres are prepared from the dispersed phase. Prior to incorporating the drug or the active agent into the dispersed phase, it is usually necessary to dissolve the active agent in a solvent. Solvents for the active agent will of course vary depending upon the nature of the agent. Typical solvents that may be used in the dispersed phase to dissolve the active agent include water, methanol, ethanol, dimethyl sulfoxide (DMSO), dimethyl formamide, dimethyl acetamide, dioxane, tetrahydrofuran (THF), acetonitrile, methylene chloride, ethylene chloride, carbon tetrachloride, chloroform, lower alkyl ethers such as diethyl ether and methyl ethyl ether, hexane, cyclohexane, benzene, acetone, ethyl acetate, and the like. Selection of suitable solvents for a given system will be within the skill in the art in view of the present disclosure.

In an embodiment of the invention, the dispersed phase is a homogeneous solution of a drug, preferably a peptide drug and a polymer in a solvent mixture. In the context of peptide-containing microspheres, impurities refer to hydrophobic impurities. Specifically, the impurities or peptide related substances referred to herein are adducts between the peptide (e.g., octreotide) and the building blocks of the polymer (e.g., PLGA monomers and oligomers). The impurity problem is more applicable, but not totally unique, to the microsphere process in which a homogeneous solution of a peptide drug and a polymer is used. It is believed that a solution of peptide and the polymer together form a favorable condition for such adduct formation because of the intimate contact between the drug and the polymer.

The hydrophobic related substances can be detected by HPLC analysis. In the case of Octreotide microspheres, hydrophobic related substances found by HPLC are octreotide related peptides formed by the reaction of amino group of octreotide and the glycolide, lactide monomers or dimers. Among the amino acids in octreotide, Lysine and the terminal amino group of “D-Phe” are responsible for these compounds. Serine may also induce some amount of impurities. Greater amount of related substances may be found with glycolide monomer and dimer compared to lactide monomer and dimer. Majority of the related substances are formed with glycolide fragments. It is believed that the glycolide may be more reactive to the amino groups. The same trend can be observed with other somastostatin analogues such as WOC4D. It is possible that microspheres with peptides having reactive amino group (such as lysine, or arginine, histidine and cystine). Further, a peptide with a free amino group as the end group of the peptide may also induce related substance formation. The impurities in such microspheres may be minimized to the acceptable levels or completely eliminated simply by practicing the present invention. Specifically, the impurities in peptide microspheres can be minimized or completely eliminated by selecting a right polymer and target load and/or by adding acids to the microsphere formulations. Target load is the theoretical drug content expressed as percentage composition of the drug in the microspheres, if all the drug were encapsulated in the microsphere. This is the percentage ratio of the drug to the total amount of drug and the polymer.

The following general cosiderations should be kept in mind in any efforts to eliminate or reduce impurities in microspheres: (i) Higher the lactide content in PLGA microsphere, lower will be the amount of related substances and the microspheres prepared from 100% PLA will have least amount of related substances; (ii) higher the PLGA molecular weight, higher will be the related substances; higher the target load in PLGA, higher will be the level of the related substances; and (iii) lower the level of extractable oligomers in PLGA, higher will be the level of related substances; hydrophobic PLGA (end blocked PLGA) can produce more related substances compared to the hydrophilic PLGA (free acid end group).

It should be noted that, besides the lactide content, the acid number of PLA or PLGA is another factor in the polymer selection step that would play role in minimizing or eliminating impurities in microspheres. Acid number of the polymer is the “mg” amount of potassium hydroxide required to neutralize the acid present in one gram of the polymer. As end blocked polymers do not have free acid group, the acid number of such end blocked polymers will be zero or negligibly small. Free acid end group polymers will have some acid number. Lower molecular weight polymers will have more acid end groups, and will have higher acid numbers. Extractable oligomer acids in microspheres may also contribute to the acid number, while not affecting the weight average molecular weight (Mw). Generally speaking, acid number shows a relationship to molecular weight, more towards the number average molecular weight. Listed below in Table 1A are some of the commonly used free acid group containing polymers in our study and their acid numbers. TABLE 1A Acid number of some polymers Polymer & % Source Lactide Lot# Mw Mn Acid No. R203H (BI) 100 86034 27325 20877 9.0 R202H (BI) 100 34038 12855 9592 14.1 100DL1AP 100 00-141-25 5626 3131 29.5 (Alkermes) 100DL1AP 100 00-141-21 7665 4136 21.5 (Alkermes) DL-PLA iv 100 D99115 6477 5296 19.9 0.11 (BPI) DL-PLA iv 100 D99120 16761 14212 9.6 0.22 (BPI) 8515 PLGA 85 X97010 16692 10217 9.4 (BPI) 8515DL2A 85 96-11-178 13924 9279 19.2 (Alkermes) 8515DL1AP 85 99-120-190 9699 6664 13.6 (Alkermes) PLGA7525H 75 76045 14279 9789 14.0 (BI) 7525DL2A 75 96-11-133 15289 10411 17.2 (Alkermes) 7525DL2A 75 1151-514 12067 6049 14.8 (Alkermes) RG504H 50 34020 41077 30157 5.9 (Alkermes) RG503H 50 281334 35151 25739 6.5 (Alkermes) RG503H 50 241802 32987 24553 7.4 (Alkermes) RG502H 50 34035 7831 4544 29.3 (Alkermes)

The acid number of PLA or PLGA polymer compositions (e.g., microspheres) may range from about 0.5 to about 50, preferably S to 40, more preferably 10 to 35. Polymers with acid numbers 40-45 may be used in short-term release formulations (e.g., for release in few days). The target load can be up to 15%. The acid number of the selected polymer for the microsphere can be under 14 if one or more specific acids are also incorporated (referred to herein as acid additive(s)) into the microsphere during the microshpere preparation process. A non-exclusive list of examples of acid additives are glacial acetic acid, lactic acid, glycolic acid and stearic acid. See the above text for examples other acids that can be used in the present invention. Accordingly, depending on the microsphere formulation, one skilled in the art having the present disclosure in hand would know how to select a polymer with a suitable acid number and the target load so that the total impurity within the peptide containing microspheres is at or below the acceptable level. If acid is added to DP, then even high MW PLGA50:50 can be used and at the same time impurity levels can be reduced to the acceptable levels or completely eliminated.

The preferred acid numbers and the target load to achieve a total impurity of less than 2% in PLGA microspheres are as follows:

In PLGA50:50 microspheres, impurity levels below 2% can be achieved by using a polymer having acid number greater than 25 and also having the target load less than 15%. In PLGA75:25 microspheres, impurity levels below 2% can be achieved by using a polymer having acid number greater than 15 and the target load less than 13%. In PLGA85:15 microspheres, impurity levels below 2% can be achieved by using a polymer having acid number greater than 12, more preferably greater than 14 and the target load less than 15%.

Microspheres thus prepared by adopting one or more of the above steps could still produce impurities during the release. For example, the following observation has been made by the present inventor(s): During the in-vitro release in phosphate buffer, at pH 7.2, the amount of these impurities increased and often exceeded 50%. In vivo study also confirmed such observation. Thus, occurrence of impurities also depends upon the pH of the release media. Release of drug in acidic environment produces less related substances compared to the release in neutral or alkaline pH. The impurity formation during the release from the PLGA/PLA could be minimized by including less water soluble acids in the microsphere. When these acids remain longer in the microsphere, they provide low pH environment resulting in lower impurities. Even with low pH environment inside the microspheres, PLGA with higher glycolide content may produce impurities. In such cases, either PLA or PLGA with glycolide content less than 25% is preferred. If an acidic environment is present inside the microspheres during in vivo release, e.g. in a tissue of an animal or human, the microspheres prepared according to the present invention may not produce significant amount of related substances. Preferred microsphere product is one formed using PLGA 85:15 or 75:25PLGA.

As already referred to above, the present invention also relates to GnRH analogue containing polymer formulations that show increased solubility of the analogue and resistance to gelling despite the presence of high levels of the analogue in the formulation. A number of GnRH analogues are known in the art. These include both agonists and antagonists of GnRH. These include, for example, orntide, antide, cetrorelix, ganirelix, abarelix, leuprolide, nafarelin, triptorelin, goserelin, buserelin, Azaline and others known in the art. See also, for example, the U.S. Pat. Nos. 5,480,969 and 5,656,727, and Jiang et al., 2001, J. Med. Chem., 44:453-467.

A high level of GnRH analogue means an amount of GnRH analogue that is no longer soluble in a solvent, even if soluble the resulting solution is unstable and gels due to the high level. The solvent referred to in this definition is one that is typically used for dissolving a GnRH analogue in preparing dispersed phase formulations. The solvents that are typically used are water, methanol, ethanol, dimethyl sulfoxide (DMSO), dimethyl formamide, dimethyl acetamide, dioxane, tetrahydrofuran (THF), methylene chloride, ethylene chloride, carbon tetrachloride, chloroform, diethyl ether, methyl ethyl ether, hexane, cyclohexane, benzene, acetone and ethyl acetate. However, most of the GnRH analogs are soluble only at certain concentrations (at very low concentrations of antagonists and moderate concentrations of agonists) beyond which these analogs pose solubility and gelling problems when dissolved in these solvents. For example, orntide, which is antagonist of GnRH, is soluble in aqueous media only at concentrations less than 5 mg/mL even at a pH lower than 5. Further, it tends to gel even at that low concentration and whereas the desired concentration of orntide in a formulation for microspheres is at least 100 mg/mL. Once orntide gels in DP, it can be very difficult to bring it back to solution. Leuprolide, which is an agonist of GnRH, is soluble at concentration of 140 mg leuprolide/mL of methanol without gelling problems. The concentration of 240 mg leuprolide/mL of methanol, however, does not form a stable solution; the solution turns hazy in few minutes to hours followed by gelling of the hazy solution.

By practicing the present invention, however, one skilled in the art can overcome problems associated with the use of high levels GnRH analogues in a formulation. Such formulations can be used to produce microspheres, implants or other types of sustained release drug delivery systems. Further, such formulations can be filtered using micro filters. Of particular importance, one would be able to obtain filter sterilizable GnRH analog containing formulations for use in the manufacture of microspheres. That is, the formulations prepared according to the present can be filtered to obtain sterile solutions. For example, the solutions prepared according to the present invention can be filtered using a 0.2μ filter.

Of the GnRH analogs, GnRH antagonists are more difficult to dissolve in solvents than GnRH agonists. As a result, GnRH antagonists may, but not necessarily, require more than a single step procedure to bring a high concentration of GnRH antagonists into a clear solution that is completely resistant to gelling, and also may require higher amount of acid. Preferred GnRH antagonists are orntide, cetrorelix, ganirelix, and abarelix and preferred GnRH agonists are leuprolide, triptorelin, and goserelin. Now, referring to orntide, a GnRH antagonist, as an example, various approaches to increase the solubility of orntide present in solvents at high levels (i.e., at levels typically used for dissolving a GnRH analogue and for preparing dispersed phase formulations are explained below.

In order to prepare a sustained release form using polyester matrix such as PLGA containing dispersed phase formulations, orntide is dissolved in a solvent or a mixture thereof with which the polymer containing solution is compatible or miscible. But, the typical formulation having, for example, methylene chloride, methanol, PLGA and orntide does not produce a stable clear solution. It forms a hazy suspension which often gels before completing the preparation of the formulation. Microspheres prepared from a hazy and gelling solution do not show consistent release characteristics. The gelling solution poses a problem for sterile filtration for aseptic manufacturing of the microsphere formulation. For example, in an attempt to obtain orntide microspheres, the present inventors prepared a dispersed phase (DP) by mixing the orntide-methanol slurry and PLA or PLGA-DCM solution. The concentration of orntide was about 1.7%. The DP thus obtained was partially clear to hazy and showed a considerable increase in viscosity even during a short period of storage (5-10 min) before dispersing it into a continuous phase (CP, 0.35% PVA solution) for making the microspheres. The DP could not be filtered through 0.22 micron filter due to the characteristics such as lack of clarity and the tendency to gel. But by practicing the present invention, the above insolubility and gelling problems can be overcome.

Stability of the orntide containing DP against gelling can be improved by adding sufficient amount of an acid or a combination of acids (an acid or a combination of acids is also referred to herein as acid additive). One skilled in the art would know what is a sufficient amount of an acid additive. For example adding glacial acetic acid to the DP can improve the stability. Lactic acid can be used instead of glacial acetic acid. Lactic acid is hygroscopic and is available as 85-90% solution in water. It should be noted that the water content in the acids in larger amount may cause phase separation. Accordingly, anhydrous acids or acids containing water at less than 5% are preferred.

Yet another step for achieving a clear dispersed phase with the minimum required amount of acid is by following a certain order of adding the solvent components to the orntide. Preferred order of addition is as follows: First, glacial acetic acid or other suitable acid is added to the orntide to form a solution. To this solution, methanol or some other suitable solvent is added; a solvent that is typically used to dissolve a GnRH antagonist or a solvent portion in which both the antagonist and the polymer are soluble (e.g., DCM) is added to form a solution before adding any other component to this solution. Then, a portion of the DCM or other solvent that is used for dissolving the polymer in the composition is added. Preparing the orntide in this manner does not require heating or warming at 40 C to achieve clear solution and also it prevents initial gelling. This solution is then added to a polymer (e.g., PLGA or PLA) solution and mixed well. Alternatively, polymer solution in suitable solvent can be added to the orntide solution in acid. This way, a clear, stable, non-gelling and filterable DP can be obtained. If any other solvent is added to orntide before adding and dissolving the orntide in an acid, the tendency to form the gel is higher.

Orntide has better solubility at low pH buffer. To achieve good drug incorporation efficiency, the CP may be buffered to, for example, pH7 to 9. The buffering capacity of CP should be high enough to neutralize the acid added to the DP formulation without dropping the pH preferably not below 6.8, certainly not below 6. This can be followed as a general method for increasing the encapsulation efficiency into microspheres of various drugs that are more soluble in acid than in basic solutions.

Another observation was that the raw material orntide prepared without the special freeze drying process may require a considerably high amount of acid additive, greater than 20%. The dispersed phase composition thus obtained may not produce microspheres with low MW polymer with desired release characteristics by O/W process, and under that situation the preferred method of making microsphere is by O/O process. Likewise, the raw material orntide that is subject to the special freeze drying followed by the addition of an acid additive may also require heating at 40° C. but the amount of acid needed is considerably low and the dispersed phase composition thus obtained produces microspheres with desired release characteristics. Thus, in the case antagonists of GnRH, the amount of acid required depends to some extent on whether the antgonist was freeze-dried or not. Adding the components in an appropriate order, however, does not require heating. As mentioned above, as part of the order, ornitde must first be dissolved in an acid before adding other components such as methanol to prepare a dispersed phase formulation. This way, dissolution of orntide or other antagonist can be achieved rapidly without any initial gelling. It will also result in a very stable solution which is easily filterable through 0.2μ filter or smaller (0.1μ, 0.5μ and so on).

The present inventors have prepared several microsphere formulations starting with the TBA freeze dried orntide as the GnRH antagonist. The solubility and gelling problems were avoided by either acid addition to the DP or with the proper order of adding components to make the DP. Both PLA or PLGA microspheres were prepared to achieve a 3 month, 6 month or 1 year release formulations.

Now, referring to leuprolide, a GnRH agonist, as an example, the approach(es) required to increase the solubility of leuprolide at high levels in solvents (i.e., at levels typically used for preparing dispersed phase formulations and microspheres) is explained. Leuprolide is more soluble than orntide in solvents such as water or methanol. However, to dissolve a high level of leuprolide one or more of the solubility increasing approaches described above with respect to orntide may be followed. In general, adding a small amount of an acid (a low pKa acid) to leuprolide or a leuprolide containing DP should in most part overcome the solubility and gelling problems. Thus, in the case GnRH agonists freeze dried agonist as a raw material or a certain order of addition of components to prepare dispersed phase may be followed, but may not be required.

In the context of GnRH analogues such as leuprolide, a trace amount of polyvalent anion in leuprolide starting material may also induce leuprolide precipitation/gelling/insolubility problems, regardless of the level of leuprolide, in dispersed phase or even in a simple leuprolide-solvent (methanol or DMSO) solution. Such impurity induced insolubility may be overcome by removing those ions using agents such as EDTA or other suitable chelating agents. The same procedure can be applied to GnRH analogues that are antagonists.

The sustained release formulations of the invention may be used for human applications as well as non-human animals, such as dogs, pigs, monkeys, rats, mouse rabbits and other animals.

EXAMPLE(S)

The following examples further illustrate the present invention. The examples below are carried out using standard techniques, that are well known and routine to those of skill in the art, except where otherwise described in detail. The examples are illustrative and do not limit the invention.

A. Molecular Weight Reduction of Polyester Matrix and its Control in Dispersed Phase Prepared with Methanol

Molecular weight reduction of PLGA in blank and a peptide containing dispersed phase prepared using methanol as a solvent and the control of the molecular weight reduction was carried out as detailed below.

1. Leuprolide as Peptide in the Dispersed Phase

Control of molecular weight reduction of PLGA in dispersed phase (DP) with leuprolide or without (i.e., blank) was studied. The DP is a solution of PLGA or PLA in solvents. The following materials and procedures were used to demonstrate control of molecular weight reduction of PLGA in dispersed phase.

Leuprolide acetate, Lot#FLEUP 9905 (Bachem, Calif.); RG503H, Lot# 290103 (Boehringer Ingelheim); RG503, Lot# 1002249 (Boehringer Ingelheim); Lactic acid, Racemic Lot# 120K1733 (Sigma) with water content 10% or lower, achieved by drying a 85-90% solution in a desiccator chamber under vacuum for a day; Glycolic acid, 98%, Ultra grade, Lot# 118H3449 (Sigma); Oligomer, obtained by degrading RG502H Lot# 34035 (BI) by higher temperature and moisture (it was a viscous dark yellow color liquid and the molecular weight by GPC showed Mw=533 and Mn=393); Dimethyl sulfoxide (DMSO), Lot# CC939 (Burdick & Johnson); Dimethylacetamide (DMAc), Lot# CS08952AS (Sigma-Aldrich); Dichloromethane (DCM), HPLC grade, Lot# BZ200 (Burdick & Johnson); Methanol (MeOH), HPLC grade, Lot# CE075 (Burdick & Johnson); Tetrahydrofuran (THF), HPLC grade, Lot# BW062, (Burdick & Johnson).

GPC Procedure: The DP samples were diluted with THF and assayed for molecular weight by GPC procedure. Specifically, the dispersed phase was diluted appropriately with THF to achieve the PLGA concentration at around 10 mg/mL. Leuprolide is not soluble in THF and will precipitate. Even if the solution appeared clear, the GPC samples were always filtered through 0.45 micron PTFE syringe filter before analysis. First few mL samples were discarded.

The columns used in the GPC procedure were Waters, Styragel HR-2, 4.6×300 mm, For MW 500-20,000, Lot# T11991, Part# WAT045865 and Waters, Styragel HR-4, 4.6×300 mm, Fot MW 5000-500,000, Lot# T13211, Part# WAT045865 connected in series. Temperature of the columns were 35° C. THF (100%) was used as a mobile phase Flow rate was 0.4 mL/min. Detector used was a refractive index detector Calibration standards were narrow molecular weight polystyrene standards from Polymer Laboratories Inc, Amherst, Mass. The polystyrene standards used had MW 283,300, MW 68,900, MW 21,000, MW 4920, and MW1260.

Peptide Extraction from DP: Leuprolide acetate from the dispersed phase was extracted after diluting the DP with DCM. To approx. 50 mg DP, added 2 mL DCM and added 9 mL 0.1 M acetate buffer, pH 4. The contents were mixed for about 1 hour using a rotating wheel. The contents were then centrifuged to obtain DCM droplets-free aqueous phase for HPLC assay.

HPLC Method: The column used in the HPLC method was C-18 Neucleosil, 4.6×250 mm, 100 Å, 5 μm from Phenomenex. Mobile Phase was (A) 0.025 M potassium phosphate, pH 5.0 (B): Acetonitrile. The gradient was 80%-50% A in 55 minutes. The column temperature was ambient and the flow Rate was 1.5 mL/min. Peak detection was at 220 nm.

The temperature during the formation of DP was 25-30° C., i.e., 25-30° C. was dissolution temperature. After the formation, the DP was filtered, and subjected to microsphere preparations or storage under appropriate temperature.

Molecular Weight Reduction in Blank DP: DPs were prepared using RG503H without including leuprolide acetate. To the DP, various acids were added as shown in Table-1B. TABLE 1B Blank Dispersed Phase Formulation with Acid Additives % Acid RG503H DCM MeOH Acid in DP* RG503H + DCM + MeOH 0.68 g 3.10 g 0.87 g 0 N.A. RG503H + DCM + MeOH + G.AA 0.68 g 3.10 g 0.87 g G. acetic acid = 0.017 g 0.4 RG503H + DCM + MeOH + LA 0.68 g 3.10 g 0.87 g Lactic acid = 0.02 g 0.4 RG503H + DCM + MeOH + GA 0.68 g 3.10 g 0.87 g Glycolic acid = 0.017 g 0.4 RG503H + DCM + MeOH + Oligomer 0.68 g 3.10 g 0.87 g Oligomer = 0.017 g 0.4 *Based on weight ratio

The DP formulation was divided into three portions and one portion was diluted in THF immediately by mixing 0.25 g DP and 3.0 mL THF. GPC was performed on these samples. The other two portions of the DP were placed in 25° C. and 40° C. stability ovens in sealed vials. After 24 hours incubation, the DP samples were diluted with THF and assayed for molecular weight by GPC. See, Table-2 for the molecular weight values of PLGA in DP incubated 25° C. or 40° C. for 24 hours. TABLE 2 Mw values of PLGA in DP 25° C.-24 Hours 40° C.-24 Hours Mw % Change % Change DP component Initial Mw in Mw Mw in Mw RG503H + DCM + 46585 38940 16.4 28476 38.9 MeOH RG503H + DCM + 45638 38329 16.0 27209 40.4 MeOH + G.AA PLGA + DCM + 46128 41853 9.3 34361 25.5 MeOH + LA PLGA + DCM + 46053 42748 7.2 34902 24.2 MeOH + GA PLGA + DCM + 46022 42283 8.1 32664 29.0 MeOH + Oligomer

There was reduction in Mw upon incubating the DP consisting of RG503H, DCM and MeOH. The presence of lactic acid, glycolic acid, and oligomer acids reduced the reduction in Mw. Under the experimental conditions, acids with very low pKa such as lactic (pKa 3.08) and glycolic (pKa 3.83) were more effective in preventing MW reduction caused by methanol. Even with a fraction of the acid (less than or equal to 1 mol % to that of the nucleophilic compound, methanol) in the dispersed phase, there was influence on the molecular weight reduction.

Molecular weight Reduction in Leuprolide DP: DPs were prepared with leuprolide acetate and with various acidic additives as shown in Table-3. TABLE 3 Leuprolide Containing Dispersed Phase Formulation with Acid Additives Leup. % Acid Molar ratio of DP components RG503H DCM MeOH Acetate Acid in DP* Acid/Leup. Ac RG503H + Leup. 0.68 g 3.10 g 0.87 g 0.17 g 0 N.A. N.A Ac + DCM + MeOH RG503H + Leup. 0.68 g 3.10 g 0.87 g 0.17 g G. acetic 0.4 2.1 Ac + DCM + MeOH + G.AA acid = 0.017 g RG503H + Leup. 0.68 g 3.10 g 0.87 g 0.17 g Lactic 0.4 1.41 Ac + DCM + MeOH + LA acid = 0.020 g RG503H + Leup. 0.68 g 3.10 g 0.87 g 0.17 g Glycolic 0.4 1.64 Ac + DCM + MeOH + GA acid = 0.017 g RG503H + Leup. Ac + + 0.68 g 3.10 g 0.87 g 0.17 g Oligomer = 0.4 0.32 DCM + MeOH + Oligomer 0.017 g *Based on weight ratio

The DP formulations were divided into three portions. One portion was used for the molecular weight determination (GPC) and leuprolide purity (HPLC). Other two portions were placed at 25° C. and 40° C. in sealed vials. After 24 hours, the molecular weight of the polymer and the purity of the leuprolide were assayed. The molecular weight of the polymer in various DP samples and the change upon storage are shown in Table 4. TABLE 4 Mw of polymer in DP and the Change 25° C.-24 Hours 40° C.-24 Hours Initial % Reduction % Reduction DP components Mw Mw in Mw Mw in Mw RG503H + Leup. Ac. + 42538 14533 65.8 5301 87.5 DCM + MeOH RG503H + Leup. Ac. + 44507 15700 64.7 5891 86.8 DCM + MeOH + G.AA RG503H + Leup. Ac. + 44969 23022 48.8 9675 78.5 DCM + MeOH + LA RG503H + Leup. Ac + 44398 26361 40.6 10825 75.6 DCM + MeOH + GA RG503H + Leup. Ac. + 43918 20593 53.1 8430 80.8 DCM + MeOH + Oligomer

As shown in Table-4, there was a considerable reduction in the molecular weight of the polymer in the DP containing leuprolide. Presence of lactic acid, glycolic acid, and oligomer acids reduced the extent of molecular weight reduction, much more efficiently compared to acetic acid.

Shown in FIG. 1 is a comparison of the Mw of the PLGA in blank and the leuprolide DP stored at 25° C. and in FIG. 2 is a comparison of the Mw reduction that occurred in the DP stored at 40° C. At 25° C., the acid additives (lactic acid, glycolic acid, and the oligomer acids) were effective in reducing the leuprolide/induced molecular weight reduction of PLGA. At 40° C., the reduction Mw of the leuprolide containing DP was very high even in the presence of the acid additive. Using higher amount of low pKa acid will be more effective in preventing the MW reduction.

2. Octreotide as a Peptide in the Dispersed Phase

Control of molecular weight reduction of PLGA in DP with octreotide or without it (i.e., blank) was also studied. Octreotide acetate is a peptide which has two free amino groups, D-Phe (1st place) and Lysine (5^(th) place). The DP is a solution of PLGA or PLA in solvents. The following materials and procedures were used to demonstrate control of molecular weight reduction of PLGA in dispersed phase with octreotide.

Octreotide acetate from Polypeptide Laboratories, Lot# PPL-OCT9901R; RG503H, Lot# 290103 (Boehringer Ingelheim); RG503, Lot# 1002249 (Boehringer Ingelheim); Lactic acid, Racemic Lot# 120K1733 (Sigma) with water content 10% or lower, achieved by drying a 85-90% solution in a desiccator chamber under vacuum for a day; Glycolic acid, 98%, Ultra grade, Lot# 118H3449 (Sigma); Oligomer, obtained by degrading RG502H Lot# 34035 (BI) by higher temperature and moisture (it was a viscous dark yellow color liquid and the molecular weight by GPC showed Mw=533 and Mn=393); Dimethyl sulfoxide (DMSO), Lot# CC939 (Burdick & Johnson); Dimethylacetamide (DMAc), Lot# CS08952AS (Sigma-Aldrich); Dichloromethane (DCM), HPLC grade, Lot# BZ200 (Burdick & Johnson); Methanol (MeOH), HPLC grade, Lot# CE075 (Burdick & Johnson); Tetrahydrofuran (THF), HPLC grade, Lot# BW062, (Burdick & Johnson).

GPC Procedure, conditions and peptide extraction from DP are the same for octreotide example as those used for the leuprolide example above.

HPLC Method: The column used was C-18 Neucleosil, 4.6×250 mm, 100 Å, 5 μm from Phenomenex and the column temperature was ambient. The mobile phase was (A) Water-0.1% TFA, (B) Acetonitrile-0.1% TFA. The gradient was 20% B to 60% B over 25 minutes. The flow rate was 1.5 mL/min. The peak detection wave length was 220 nm.

Molecular Weight Reduction in Blank Dispersed Phase: The Dispersed Phases were prepared using RG503H without including octreotide acetate. To the DP, various acids were added as shown in Table-5. TABLE 5 Blank Dispersed Phase Formulation with Acid Additives DP % Acid components RG503H DCM MeOH Acid in DP PLGA + DCM + MeOH 0.77 g 3.71 g 0.87 g 0 N.A. PLGA + DCM + MeOH + G.AA 0.77 g 3.71 g 0.87 g G. Acetic acid = 0.037 g 0.7 PLGA + DCM + MeOH + 0.77 g 3.71 g 0.87 g G. Acetic Acid = 0.073 g 1.5 G.AA + Pam.A Pamoic acid = 0.037 g 0.7 PLGA + DCM + MeOH + LA 0.77 g 3.71 g 0.87 g Lactic acid = 0.044 g 0.7 PLGA + DCM + MeOH + GA 0.77 g 3.71 g 0.87 g Glycolic acid = 0.037 g 0.7 PLGA + DCM + MeOH + Oligomer 0.77 g 3.71 g 0.87 g Oligomer = 0.037 g 0.7

The DP formulation was divided into three portions and one portion was diluted in THF immediately by mixing 0.25 g DP and 3 mL THF. GPC was performed on these samples. Two other portions of the DP were placed in 25° C. and 40° C. stability ovens in sealed vials. After 24 hours incubation, the DP samples were diluted with THF and assayed for molecular weight by GPC. See, Table-6 for the molecular weight values of PLGA in DP incubated 25° C. or 40° C. for 24 hours. TABLE 6 Mw values of PLGA in DP 25° C.-24 Hours 40° C.-24 Hours Mw % Change % Change DP components Initial Mw in Mw Mw in Mw RG503H + 51807 41448 20.0 28225 45.5 DCM + MeOH RG503H + 49881 41787 16.2 27020 45.8 DCM + MeOH + G.AA RG503H + 50739 40244 20.7 28914 43.0 DCM + MeOH + G.AA + PA PLGA + DCM + 51692 47071 8.9 38111 26.3 MeOH + LA PLGA + DCM + 51269 46525 9.3 38393 25.1 MeOH + GA PLGA + DCM + 53052 46389 12.6 35847 32.4 MeOH + Oligomer

As shown in Table-6, lactic acid and glycolic acid provided good protection for PLGA against molecular weight reduction followed by Oligomer acid.

Molecular weight Reduction in Octreotide Containing DP: Dispersed Phases were prepared with octreotide acetate and with various acidic additives as shown in Table-7. TABLE 7 Octreotide Acetate Containing Dispersed Phase Formulation with Acid Additives DP Octreotide % Acid components RG503H DCM acetate MeOH Acid in DP RG503H + Oct. Act. + 0.77 g 3.71 g 0.096 g 0.87 g 0 N.A. DCM + MeOH RG503H+ Oct. Act + DCM + 0.77 g 3.71 g 0.096 g 0.87 g G. acetic acid = 0.038 g 0.7 MeOH + G.AA RG503H + Oct. Act + DCM + 0.77 g 3.71 g 0.096 g 0.87 g G. acetic acid = 0.074 g 1.5 MeOH + G.AA + Pam.A Pamoic acid = 0.038 g 0.7 RG503H + Oct. Act + DCM + 0.77 g 3.71 g 0.096 g 0.87 g Lactic acid = 0.045 g 0.7 MeOH + LA RG503H + Oct. Act + DCM + 0.77 g 3.71 g 0.096 g 0.87 g Glycolic acid = 0.038 g 0.7 MeOH + GA PLGA + Oct. Act. + DCM + 0.77 g 3.71 g 0.096 g 0.87 g Oligomer = 0.038 g 0.7 MeOH + Oligomer Note: Mole ratio of Acid to the MeOH is same as shown in Table 5

The DP formulations were divided into three portions. One portion was used for the molecular weight determination by GPC and Octreotide purity by HPLC. The other two portions were placed at 25° C. and 40° C. in sealed vials. After 24 hours, the molecular weight of the polymer and the purity of the octreotide were assayed. The molecular weight of the polymer in various DP samples and the change upon storage are shown in Table-8. TABLE 8 Mw values of PLGA in DP 25° C.-24 Hours 40° C.-24 Hours Mw % Change % Change DP components Initial Mw in Mw Mw in Mw RG503H + DCM + 42512 14539 65.8 7085 83.3 Octreotide + MeOH RG503H + DCM + 45061 16931 62.4 7222 84.0 MeOH + Octreotide + G.AA RG503H + DCM + 47509 23952 49.6 10353 78.2 MeOH + Octreotide + G.AA + PA RG53H + DCM + 51207 31317 38.8 14869 71.0 MeOH + Octreotide + LA RG503H + DCM + 49888 33026 34.8 16018 67.9 MeOH + Octreotide + GA RG503H + DCM + 50427 31594 37.4 16363 67.6 MeOH Octreotide + Oligomer

As shown in Table-8, there was a considerable reduction in molecular weight of the polymer in the DP containing octreotide without the acid(s).

Shown in FIG. 4 is a comparison of the Mw change of the PLGA in blank and Octreotide DP stored at 25° C. and in FIG. 5 is a comparison of the Mw change of the PLGA in blank and Octreotide DP stored at 40° C. Octreotide caused molecular weight reduction in PLGA, and the presence of strong acids even in small amounts controlled the molecular weight reduction. At 25° C., the acid additives (lactic acid, glycolic acid, and the oligomer acids) helped the leuprolide induced molecular weight reduction of PLGA. At 40° C., the reduction in Mw of the PLGA in Leuprolide containing DP was very high even in the presence of the acid additives.

B. Molecular Weight Reduction of Polyester Matrix and its Relationship to Peptide-Polymer Adduct Formation in DP

Molecular weight reduction of PLGA in DP containing a peptide with nucleophilic group(s), led to the proportional increase in the formation of adducts between the peptide and the polymer material (also referred to herein as related substance or the conjugates).

1. Leuprolide DP:

Leuprolide extracted from the incubated DP was assayed by HPLC to determine the adduct content. Multiple adducts from the different fragments of PLGA were observed. These adducts eluted after the leuprolide peak. Shown in Table-9 is leuprolide related substance content in the incubated DP samples. TABLE 9 Leuprolide Related Substance Content in the Incubated DP Samples 25° C. 40° C. for 24 for 24 DP components Initial Hours Hours RG503H + Leup. + DCM + 0 1.19 5.23 MeOH RG503H + Leup. + DCM + 0.05 0.35 2.18 MeOH + G.AA RG503H + Leup + DCM + 0.05 0.15 0.63 MeOH + LA RG503H + Leup + DCM + 0.05 0.15 0.46 MeOH + GA RG503H + Leup + DCM + 0.05 0.15 0.93 MeOH + Oligomer While the DP containing glacial acetic acid as acid additive slowed the related substance formation, the DP containing lactic acid or glycolic acid showed considerable reduction in related substance formation. Also, a clear relationship was noted between the molecular weight reduction and the related substance formation as illustrated in FIG. 3. Specifically, an exponential increase in the related substance formation to that of the molecular weight reduction was noted.

2. Octreotide DP

Impurity formation due to the nucleophilic attack of peptides on PLGA is another problem, which affects the quality of the peptide containing microspheres. Octreotide extracted from incubated DP were assayed by HPLC to determine the adduct content. It was shown previously that these adducts elute after the Octreotide peak, and that there will be multiple adducts formed from the different fragments of PLGA interacting with the two reactive amino groups, D-Phe end group and Lysine. Hereafter, these hydrophobic impurities will be referred to as Octreotide related substances.

DP samples shown in Table-7, incubated at 25° C. and 40° C. were assayed for the related substance content and compared to the initial samples without incubation. Comparative data is shown in Table-10 below. TABLE 10 Octreotidee Related Substance Content in the Incubated DP Samples 25° C. 40° C. for 24 for 24 DP components Initial Hours Hours RG503H + DCM + Octreotide + 0 13.95 47.59 MeOH RG503H + DCM + MeOH + 0 3.04 23.30 Octreotide + G.AA RG503H + DCM + MeOH + 0 0.95 8.10 Octreotide + G.AA + PA RG53H + DCM + MeOH + 0 1.24 4.31 Octreotide + LA RG503H + DCM + MeOH + 0 0.99 2.68 Octreotide + GA RG503H + DCM + MeOH 0 0.22 6.04 Octreotide + Oligomer FIG. 6 shows the relationship between the Mw reduction in PLGA and the related substance formation. There is a relationship between the related substance formation to the molecular weight reduction. Including low pKa acids helped reducing the related substance. C. Microspheres Prepared from Incubated DP with and Without an Acid Additive

As shown above that the molecular weight of PLGA and purity of the leuprolide were affected by storing DP even at 25° C.

Shown here is the effect of storing DP on drug load and drug encapsulation efficiency. Two dispersed phases were prepared. See, Table-6. Soon after the preparation of the dispersed phase, approximately 0.125 g was removed to follow the Mw of the PLGA and approximately 0.025 g was removed to follow the purity of Leuprolide. The remaining DP was placed at 30° C. for 16 hours (overnight) in a sealed container. After the storage, a small portion of the DP was removed to determine the Mw of PLGA and the purity of Leuprolide as performed initially. The remaining DP was subjected to the microsphere formulations. TABLE 11 Dispersed Phase Formulations for Leuprolide Microspheres Component Leup DP Leup DP + LA RG503H 4.12 g 4.11 g Leuprolide acetate 0.99 g 0.99 g DCM 18.93 g 18.74 g MeOH 5.27 g 5.27 g Lactic acid 0 0.114 g % Lactic acid based on N.A 2.7% RG503H weight

TABLE 12 Properties of the DP before and after storage Property Leup DP Leup DP + LA Mw initial 46585 46128 Leuprolide Related Substances - initial 0 0 Mw after storage 14326 28359 % Reduction in Mw 69.2% 38.5% Leuprolide Related Substances after storage 0.53 0

As shown in Table 12 both DP formulations showed lower molecular weight for the PLGA but the presence of lactic acid in the DP reduced the molecular weight reduction, and prevented the formation of related substances.

Properties of the microspheres prepared from the stored DP were compared to the typical property achieved for a microsphere prepared from non-stored DP. See, Table 13. TABLE 13 Properties of the Microspheres GJ040302 (MS GJ040902 (MS Property of prepared from stored prepared from stored a typical Property “Leup DP”) “Leup DP with LA” MS batch Drug Load, %  5.6 ± 0.35% 4.33±%  14-16 Drug encapsulation   31%   24% 78-89 efficiency, % % Leuprolide Related 6.04 ± 0.30% 0  2-4% Substances* % Drug in to CP soon 14.7% 17.7%  ≈7% after MS formation % Drug found in CP- 50.9% 58.2% ≈10% final *By extracting the drug in acetate buffer

The incorporation of lactic acid eliminated the related substance in the microspheres. The leuprolide DP which did not contain lactic acid showed 0.53% related substance initially, and increased to 6.04%. The related substance formation was gradual for leuprolide microspheres prepared from a fresh DP that did not contain lactic acid (data not shown). Lactic acid in the DP protected leuprolide from related substance formation during the entire microsphere process.

D. Effect of Solvent Used to Prepare DP on Molecular Weight Reduction of Polymer

DP formulations, as shown in Table-14, were incubated for 24 hours at 25° C. and at 40° C. to see the effect of DMSO and DMAc on molecular weight reduction compared to methanol. A DP, simply containing DCM and PLGA was also included in the experiment for comparison. TABLE 14 DP Composition with Variety of Solvents DP Code RG503H DCM Other Solvent RG503H + DCM 0.85 g 3.87 g 0 RG503H + DCM + MeOH 0.85 g 3.87 g MeOH: 1.12 g RG503H + DCM + DMSO 0.85 g 3.87 g DMSO: 1.12 g RG503H + DCM + DMAc 0.85 g 3.87 g DMAc: 1.12 g

The DP samples were incubated at 40° C. for 24 hours in sealed tubes. The molecular weight of the PLGA after incubation was as shown in Table-15. TABLE 15 Mw and the Reduction Mw of PLGA Upon Incubation - Effect of Solvent Mw RG503H + DCM 52257 RG503H + DCM + MeOH 25907 RG503H + DCM + DMSO 52150 RG503H + DCM + DMAc 52876

As shown in Table 15, the Mw of RG503H in the DP system free from methanol remains unaffected. Leuprolide containing DP with DMSO instead of methanol is the appropriate system to compare the effect of various acids on preventing the leuprolide induced nucleophilic attack of PLGA ester bonds.

DP samples listed in Table 16 were prepared and incubated at 25 and 40° C. for 24 hours. Both molecular weight and the leuprolide impurity were followed. TABLE 16 DP formulations prepared with DMSO solvent Leup. Acid % acid based DP components RG503H DCM Act. DMSO additive on total DP RG503H + Leup. Ac. + DMSO 0.85 g 3.87 g 0 1.52 g 0 N.A RG503H + Leup. Ac. + DMSO + G.AA-1 0.85 g 3.87 g 0.21 g 1.52 g GAA: 0.022 g 0.35 RG503H + Leup. Ac.. + DMSO + G.AA-2 0.85 g 3.87 g 0.21 g 1.52 g GAA: 0.044 g 0.70 RG503H + Leup. Ac.. + DMSO + LA-1 0.85 g 3.87 g 0.21 g 1.52 g LA: 0.026 g 0.35 RG503H + Leup. Ac. + DMSO + LA-2 0.85 g 3.87 g 0.21 g 1.52 g LA: 0.052 g 0.70 RG503H + Leup. Ac. + DMSO + GA-1 0.85 g 3.87 g 0.21 g 1.52 g GA: 0.022 g 0.35 RG503H + Leup. Ac. + DMSO + GA-2 0.85 g 3.87 g 0.21 g 1.52 g GA: 0.044 g 0.70 RG503H + Leup. Ac. + DMSO + Oligomer-1 0.85 g 3.87 g 0.21 g 1.52 g Oligomer: 0.022 g 0.35 RG503H + Leup. Ac. + DMSO + Oligomer-2 0.85 g 3.87 g 0.21 g 1.52 g Oligomer: 0.044 g 0.70

Table-17 shows the Mw values before and after incubating the DP and compares the percentage loss in Mw. TABLE 17 Mw Change Upon Storing DMSO Containing Leuprolide DP 25° C.-24 Hours 40° C.-24 Hours % Reduction % Reduction DP components Initial Mw Mw in Mw Mw in Mw RG503H + Leup. Ac. + DMSO 44564 39155 12.1 23470 47.3 RG503H + Leup. Ac. + DMSO + G.AA-1 45925 40724 11.3 28063 38.9 RG503H + Leup. Ac.. + DMSO + G.AA-2 47019 42045 10.6 27897 40.7 RG503H + Leup. Ac.. + DMSO + LA-1 46581 41816 10.2 32804 29.6 RG503H + Leup. Ac. + DMSO + LA-2 46101 41515 9.9 32503 29.5 RG503H + Leup. Ac. + DMSO + GA-1 46470 40435 13.0 24864 46.5 RG503H + Leup. Ac. + DMSO + GA-1 47399 37954 19.9 23612 50.2 RG503H + Leup. Ac. + DMSO + Oligomer-1 47080 41951 10.9 34281 27.2 RG503H + Leup. Ac. + DMSO + Oligomer-2 47463 43196 9.0 35648 24.9

Thus, the storage of DP at 25° C. caused approximately 11% reduction in Mw. Acid additives showed very little or no protection against Mw reduction. It is surprising to find that glycolic acid did not provide any protection against molecular weight reduction.

Table-18 compares the molecular weight reduction occurred in leuprolide DP containing methanol to that containing DMSO. TABLE 18 Mw of polymer in DP and the Change 25° C.-24 Hours 40° C.-24 Hours Initial % Reduction % Reduction DP components Mw Mw in Mw Mw in Mw RG503H + Leup. Ac. + DCM + MeOH 42538 14533 65.8 5301 87.5 RG503H + Leup. Ac. + DCM + DMSO 44564 39155 12.1 23470 47.3 RG503H + Leup. Ac. + DCM + MeOH + G.AA 44507 15700 64.7 5891 86.8 RG503H + Leup. Ac. + DCM + DMSO + G.AA 45925 40724 11.3 28063 38.9 RG503H + Leup. Ac. + DCM + MeOH + LA 44969 23022 48.8 9675 78.5 RG503H + Leup. Ac. + DCM + DMSO + LA 46581 41816 10.2 32804 29.6 RG503H + Leup. Ac + DCM + MeOH + GA 44398 26361 40.6 10825 75.6 RG503H + Leup. Ac + DCM + DMSO + GA 46470 40435 13.0 24864 46.5 RG503H + Leup. Ac. + DCM + MeOH + Oligomer 43918 20593 53.1 8430 80.8 RG503H + Leup. Ac. + DCM + DMSO + Oligomer 47080 41951 10.9 34281 27.2

Thus, the Mw reduction induced by methanol was much higher compared to the Mw reduction induced by leuprolide acetate.

The DP samples were also followed for the related substance formation. Table-19 compares the related substance formed in the DMSO containing DP incubated for 24 hours. TABLE 19 Related Substance Formation in Leuprolide DP Containing DMSO 25° C. 40° C. for 24 for 24 Initial Hours Hours RG503H + Leup.Ac. + DCM + 0 3.00 18.55 DMSO RG503H + Leup. + DCM + 0 1.39 8.46 DMSO + G.AA-1 RG503H + Leup. + DCM + 0 0.98 6.49 DMSO + G.AA-2 RG503H + Leup + DCM + 0 0.34 1.80 DMSO + LA-1 RG503H + Leup + DCM + 0 0 1.48 DMSO + LA-2 RG503H + Leup + DCM + 0 0 0.56 DMSO + GA-1 RG503H + Leup + DCM + 0 0 0.24 DMSO + GA-2 RG503H + Leup + DCM + 0 0.18 1.61 DMSO + Oligomer-1 RG503H + Leup + DCM + 0 0.28 1.15 DMSO + Oligomer-2

As shown in Table-19, the DP without acid additive produced higher amount of related substance in presence of DMSO. Mw reduction was less in the DMSO containing DP, because the ester bond cleavage was by leuprolide acetate only. Ester bond cleavage induced by leuprolide acetate could be associated with related substance formation. Methanol may be competing with leuprolide acetate for the ester bond cleavage thereby producing less related substance. Also, there is a possibility that methanol may be converting back the leuprolide related substance to leuprolide. Presence of small amount of acid reduced the related substance formation considerably. There was no relationship between the Mw reduction and the related peptide formation in the presence of DMSO in DP.

E. Microspheres with DP Having Methanol or DMSO

Leuprolide acetate loaded PLGA microspheres were prepared by a solvent extraction procedure. Briefly, leuprolide acetate (0.3 g) and acetic acid (0.15 g) were dissolved in either MeOH (1.8 g) or DMSO (1.8 g). The solutions were then combined with a solution containing polymer (2.7 gm RG503H) in DCM (9 g). The DP samples thus prepared were stored in sealed containers at 25° C. for 24 hours.

Microspheres were prepared by dispersing the DP formulations in an aqueous solution containing 0.35% (wt/vol.) polyvinyl alcohol (continuous phase (CP)) using a homogenizer such as a Silverson Homogenizer (Silverson Machines, Waterside UK). The microsphere suspension thus formed was transferred to a 3-liter solvent removal vessel to complete solvent removal. The suspension was then filtered, washed and dried overnight at ambient temperature.

Two leuprolide containing microsphere batches were made using RG503H, with methanol in the dispersed phase, and with DMSO in the dispersed phase.

The methanol containing DP was prepared by mixing a solution of 2.7 g RG503H in 9 g DCM, and a solution of 0.3 g leuprolide acetate (pure) in 0.15 g glacial acetic acid and 1.8 g methanol.

The DMSO containing DP was prepared by mixing a solution of 2.7 g RG503H in 9 g DCM, and a solution of 0.3 g leuprolide acetate (pure) in 0.15 g glacial acetic acid and 1.8 g DMSO.

The DP samples thus prepared were stored in a sealed container at 25° C. for 24 hours. Microsphere batch BT040303 was prepared using the DP containing methanol which was stored for 24 hours, and the Batch GJ040303 was prepared using the DP containing DMSO which was also stored for 24 hours.

Microsphere was prepared by dispersing the DP in to 1.5 lit CP, which is a 0.35% PVA solution. The dispersion was achieved using a Silverson homogenizer, by stirring at 5000 RPM. While stirring the CP, DP was delivered, just below the homogenizer head. The microsphere suspension thus formed was transferred in to a 3 liter jacketed bioreactor (Applikon) stirring at 800 RPM. The suspension was heated to 40° C. along with air sweep for the complete removal DCM. The suspension was cooled back to the ambient temperature, filtered, washed with plenty of water, and dried overnight under vacuum at ambient temperature.

Properties of the two microsphere batches were as shown in Table 20 below. TABLE 20 Properties of the microspheres. Property BT040303 GJ040303 Components in the DP DCM, MeOH, Leuprolide DCM, DMSO, Leuprolide acetate, RG503H, Glacial acetate, RG503H, Glacial acetic acid acetic acid Target Load of Leuprolide 10% 10% acetate in the microsphere Actual Leuprolide content 8.506 ± 0.002 9.093 ± 0.002 by assay Drug encapsulation 85% 91% efficiency, % % Related Substance in the 1.83 ± 0.28 1.39 ± 0.04 microsphere Molecular weight of the Mw: 18983 Mw: 35789 polymer in the microsphere Mn: 7771 Mn: 15690 % Yield 77% 71% Bulk density, g/mL 0.82 0.41 Note: Molecular weight (Mw) of the raw polymer RG503H used for the batches was: 40812 and Mn: 19491.

Microspheres prepared with both DMSO and methanol in the DP had good drug encapsulation efficiency. The bulk density of the microsphere prepared with DMSO is higher, probably due to the DMSO being a good solvent for the polymer, which does not cause polymer to precipitate in the DP droplets.

Both microsphere batches were prepared from a DP which contained glacial acetic acid. Hence the amount of related substance in the microsphere is comparatively low, even though these microspheres are prepared with the stored DP (compare with Table-13).

F. Octreotide Microspheres

1. Preparation of the Microspheres

Octreotide acetate loaded PLGA and PLA microspheres were prepared by a solvent extraction procedure. Briefly, octreotide acetate was dissolved in methanol, and combined with a polymer/methylene chloride solution. The subsequent octreotide/polymer mixture (dispersed phase) was then dispersed in an aqueous solution containing 0.35% (wt/vol.) polyvinyl alcohol (continuous phase (CP)) using a homogenizer such as a Silverson Homogenizer (Silverson Machines, Waterside UK). The microsphere suspension thus formed was transferred to a 3-liter solvent removal vessel to complete solvent removal. The suspension was then filtered, washed and dried overnight at ambient temperature.

Various Octreotide microspheres were prepared from a clear dispersed phase containing the polymer, octreotide, methylene chloride (DCM) and methanol. Octreotide acetate was obtained from Polypeptide Laboratories or Peninsula Lab. Polymer concentration was varied for the batches to obtain appropriate particle size and also to obtain efficient drug load. Methanol (MeOH) to DCM ratio was increased while making higher drug load batches to get a clear dispersed phase. The continuous phase was a 0.35% PVA solution in all preparations. In a typical preparation, CP was taken in a beaker and stirred using a Silverson homogenizer (standard emulsor screen). To the stirring CP, the dispersed phase was added just below the Silverson head using a laboratory syringe with a bent needle. After 30 sec to 1 minute homogenization, the entire suspension was transferred into a 3 liter Applikon bioreactor for solvent removal. The solvent removal from the microsphere was achieved by initial CP replacement with water followed by heating the suspension at 40° C. along with air sweep. After the solvent removal the microspheres were collected on a filter membrane, washed and dried under vacuum.

Batch size 3 g and above were prepared by a continuous flow process. Dispersed phase and the CP were administered into a in-line mixture, while stirring the microsphere suspension was collected in a Applikon bioreactor and the solvent removal was performed as described previously, for example, in the U.S. Pat. No. 5,945,126. The preparation parameters of the octreotide microspheres were as summarized in Table-21. TABLE 21 Preparation Parameters of the Octreotide Microspheres Strrring L:G Dispersed Phase Components (g) Target Speed, Batch Batch Polymer Ratio, % Mw Polymer Octreotide DCM MeOH CP Load % RPM size, g BT120798 RG503H 50:50 30,000 2.0 0.25 9.66 1.10 1500 11.1 5500 2.25 BT121198 RG502H 50:50 8,500 2.4 0.36 5.1 0.51 1500 13.0 5500 2.75 BT011599 RG503H 50:50 30,000 2.0 0.38 9.66 1.10 1500 16.0 6000 2.4 BT020999 RG503 50:50 32,000 2.22 0.28 9.66 1.10 1500 11.1 5500 2.5 BT021799 RG504H 50:50 41,000 1.78 0.22 9.0 0.9 1800 11 5500 2.0 MG090899 PLGA75:25H 75:25 14,000 1.74 0.26 8.3 2.1 1300 13.0 7000 2.0 MG091099 RG503H 50:50 30,000 1.74 0.26 8.3 0.83 1300 13.0 7000 2.0 MG092299* RG503H 50:50 30,000 1.7 0.3 8.3 0.83 1300 15.0 7000 2.0 GJ032400 50:50DL2.5A 50:50 24,000 2.25 0.25 7.5 0.75 1500 10 7000 2.5 GJ032700 75:25DL2.5A 50:50 24,000 2.20 0.30 7.5 0.75 1500 12 6500 2.5 GJ032800 75:25DL3A 75:25 39,000 1.16 0.29 5.22 0.522 1000 20 6500 2.5 GJ033100 50:50DL2.5A 100:0 24,000 2.10 0.40 6.0 0.90 1200 16 6500 2.5 GJ040300 85:15DL2A 85:15 14,000 2.175 0.325 6.5 0.85 1300 13 6500 2.5 GJ040500 75:25DL2.5A 75:25 24,000 1.837 0.363 6.0 0.9 1200 16.5 6500 2.5 GJ042700 85:15DL2A 85:15 14,000 1.8 0.2 5.0 0.6 1000 10.0 6500 2.0 GJ050100 PLGA85:15 85:15 17,000 1.78 0.22 5.5 0.66 1100 11 6500 2.0 GJ050300 90:10PLGA 90:10 6500 1.78 0.22 4.0 0.48 1000 11 6000 2.0 GJ050800 PLA iv 0.11 100:0 7000 1.78 0.22 3.8 0.45 950 11 6000 2.0 GJ050900 100DL2A 100:0 14,000 1.55 0.25 4.2 0.75 1000 14 6000 1.8 GJ051100 85:15DL2A 85:15 14,000 1.53 0.27 4.5 0.72 1000 15 6000 1.8 GJ051600 RG502H 50:50 8,500 1.80 0.20 4.5 0.5 1000 10 6000 2.0 GC122001 7525DL2A 75:25 12,000 2.625 0.375 9.0 0.9 1500 12.5 6000 3.0 *CP is 0.35% PVA with pH 7.2 buffer

2. Peptide-Polymer Adducts (or Hydrophobic Related Substances) in the Octreotide Drug Containing Microspheres

The drug content was determined by dissolving the dry microspheres in DCM and extracting the drug into acetate buffer, pH 4.0. The extract from most of the microsphere batches showed hydrophobic impurities (hydrophobic compared to octreotide) to a varying amount. It was found that incubating these microspheres at pH 37° C. in pH 7.4 phosphate buffer enhanced these impurities, especially from a PLGA50:50 polymer. The structure of the hydrophobic related substances was determined by HPLC-MS/MS. Octreotide extract from RG503H microspheres that had been incubated at 37° C. for about two weeks in phosphate buffer pH 7.4 was analyzed. Shown in FIG. 7 is a HPLC Chromatogram of Octreotide Extract with Peak Identity. The HPLC chromatogram of the extracted drug showed additional peaks appearing after the octreotide peak. Table-22 lists the structure of the related substances. Most of the peaks are related substances formed with glycolide segment. It is obvious from this analysis that the PLGA with more glycolide content produced more impurities. The level of total impurity found in each of the batches (i.e., sum of the related substances eluted after octreotide peak) is listed in Table-23. TABLE 22 The Structure of Related Substances Identified in FIG.-7 Peak No. from HPLC (See, FIG. 1) Structure 1 H-D-Phe-Cys-Phe-D-Trp-Lys-Thr-Cys- Thr-ol (Octreotide) 2 H-D-Phe-Cys-Phe-D-Trp-[Lys + G]-Thr- Cys-Thr-ol  3a H-D-Phe-Cys-Phe-D-Trp-[Lys + G − G]- Thr-Cys-Thr-ol  3b H-D-Phe-Cys-Phe-D-Trp-[Lys + L]-Thr- Cys-Thr-ol 4 H-D-Phe-Cys-Phe-D-Trp-[Lys + G − G − G]-Thr-Cys-Thr-ol 6 H-D-Phe-Cys-Phe-D-Trp-[Lys + L − G]- Thr-Cys-Thr-ol 7 H-D-Phe-Cys-Phe-D-Trp-[Lys + L − L]- Thr-Cys-Thr-ol 8 H-D-[Phe + G]-Cys-Phe-D-Trp-Lys-Thr- Cys-Thr-ol 9 H-D-[Phe + G]-Cys-Phe-D-Trp-[Lys + G]-Thr-Cys-Thr-ol 11  H-D-[Phe + G]-Cys-Phe-D-Trp-[Lys + G − G]-Thr-Cys-Thr-ol

TABLE 23 Percentage Related substances Eluted after Octreotide peak in HPLC % Mw Target % Total Batch Polymer Lactide (Approx) Load, % Impurities Acid# BT021799 RG504H 50 41,000 11 7.91 5.9 BT020999 RG503 50 32,000 11.1 14.03 0.5 BT120798 RG503H 50 30,000 11.1 6.71 7.4 BT011599 RG503H 50 30,000 16.0 10.99 7.4 MG091099 RG503H 50 30,000 13.0 9.24 7.4 MG092299 RG503H 50 30,000 15.0 11.73 7.4 GJ042800 RG503H 50 30,000 11.1 7.21 7.4 GJ032400 50:50DL2.5A 50 24,000 10 5.88 15.2 GJ033100 50:50 DL2.5A 50 24,000 16 10.11 15.2 BT121198 RG502H 50 8,500 13.0 1.38 29.3 GJ051600 RG502H 50 8,500 10 0.92 29.3 GJ032800 75:25DL3A 75 39,000 20 11.38 6.7 GJ032700 75:25DL2.5A 75 24,000 12 7.98 11.0 GJ040500 75:25DL2.5A 75 24,000 16.5 8.35 11.0 GC122001 7525DL2A 75 12,000 12.5 1.76 14.8 MG090899 PLGA75:25H 75 14,000 13.0 2.87 14.0 GJ050100 PLGA85:15 85 17,000 11 3.73 9.4 GJ040300 85:15DL2A 85 14,000 13 0.65 19.2 GJ042700 85:15DL2A 85 14,000 10.0 0.1 19.2 GJ051100 85:15 DL2A 85 14,000 15 1.96 19.2 GJ050300 90:10 PLGA 90 6500 11 0.15 31.0 GJ050900 100DL2A 100 14,000 14 0.54 22.2 GJ050800 PLA iv 0.11 100 7000 11 0.23 19.9

3. Effect of PLGA Molecular Weight on Related Substances in Octreotide Microspheres

The effect of molecular weight on related substances formation has been demonstrated using PLGA 50:50 and PLGA 75:25 octreotide microspheres. Target loads for these batches were similar. There was a relationship between the molecular weight of the polymer and the level of the related substances. See FIG. 8. More related substances were found in the microspheres prepared from high molecular weight polymers.

4. Effect of Target Load on Related Substances in Octreotide Microspheres

Target load, like the molecular weight, showed a direct relationship to related substances formation. Batches were prepared with three PLGAs with varying target load. There was a clear relationship between the amount of related substances formed versus target load. The data is shown in FIG. 9.

5. Effect of Co-Monomer Ratio on Related Substances

The comonomer ratio had very significant influence on related substances formation. Among the polymers tested, PLGA 50:50 showed the maximum related substances as shown in Table-23 above. Comparing the related substances of the batches prepared with similar molecular weight polymers it is clear that increased glycolic acid content in the polymer increased the level of related substances. See, FIG. 10.

6. Extractable Acid And Related Substances

The effect of extractable acid on related substances showed an inverse relationship (See the data below in Table 24). TABLE 24 Relationship between Extractable Acid (Mole %) and Related Substances (%) Polymer, Mw and Target Extractable Related Batch Manufacturer Load, % acid, Mole % Substances, % GJ050100 85:15 PLGA from BPI 11 0.0025 3.73 GJ042700 85:15 PLGA from Alkermes 10 0.01 0.1

Extractable acid in polymer was determined by dissolving the known amount of polymer in DCM, extracting the water soluble fractions in water, and titrating against standard alkali.

7. Effect of Polymer End Group

A batch of microspheres were prepared with an end-blocked polymer. Even though there is no free acid end group in the polymer, there may be a few acid end groups initially or there could be some additional acid end groups formed upon polymer storage prior to microsphere formulation and during microsphere formation by ester bond cleavage. Comparison of the similar Mw polymers with acid end groups and end-blocked groups showed that the end-blocked polymer produced more related substances than the polymer with acid end groups as shown in the Table 25 below. TABLE 25 Effect of End group on Related substances Formation Acid Target Related Polymer Mw Number Load, % substances, % Batch RG503 32,000 <1 11 14.06 BT020999 RG503H 30,000 7.4 11 6.71 BT120798

8. Effect of the Acid Number of the Polymer on Related Substance Formation

The acid number of the polymer is inversely related to the amount of impurity in the microsphere. Shown in FIG. 11 is the relationship between the acid number and the percentage of impurities for the microspheres prepared from PLGA50:50 having a target load 10-12% (FIG. 11A) and from other polymers having a target load 10-13% (FIG. 11B).

9. Related Substance Formation During the Various Stages of Microsphere Preparation Process

Batch GJ042800 was prepared from RG503H and portions of the microsphere suspension were removed during various stages. The microspheres were filtered on 1.2 micron membrane filter and air dried on the filter itself. The microspheres (partially dry) were dissolved in DCM and the drug was extracted in acetate buffer. The level of related substances found at various stages are shown in Table-26 below. TABLE 26 Percentage Related substances Found During Various Stages of Microsphere Formation Time from DP % Related Preparation Stage formation, min substances Dispersed Phase (before forming MS) 0 0.30 Soon after MS formation 5 1.78 After RT water exchange 25 2.61 After heating ramp 74 4.55 30 minutes at solvent removal 104 6.02 60 minutes at solvent removal 134 6.58 Final microsphere 181 7.21 Dispersed Phase (stored at 40 C. for 4 hours) 240 2.64 Or 5.07

The related substances formed as the microsphere preparation process proceeded. In the dispersed phase only a small amount of related substances were found (0.3%). Soon after the microspheres were formed the related substances increased to 1.78%. There was a raise in related substances by heating the suspension to 40° C. and during solvent removal more related substances formed. Storing the dispersed phase at 40° C. did increase the related substances from 0.3% to at 2.86% or more. The retention times and levels of the individual related substances were also studied (data not shown).

10. Effect of Adding Acids to the Dispersed Phase on Related Substance Formation

To 1.5 mg octreotide added 20 mg PLGA/PLA and dissolved in 0.5 mL DCM and 0.1 mL methanol. To this, 10 mg of glacial acetic acid, triethylamine, 85% lactic acid, glycolic acid or stearic acid was added. Samples were placed at 40° C. for 24 hour and 48 hour period. Followed by that to the sample added 2 mL DCM and extracted the drug in 0.1 M acetate buffer and assayed by HPLC. The samples included in the study are listed in Table 27.

The hydrophobic related substances found in these samples after 24 and 48 hour period are shown in FIG. 12. Elution of control sample showed substances that are impurities (2.5%) but not related substances, and few of those impurities were also found in the standard octreotide. Presence of RG503H increased the related substances to 4-7%. A repeat of the RG503H study showed up to 18% related substances in 48 hour incubation. Presence of lactic acid to the RG503H system reduced the related substances and made comparable to the control. Glycolic acid also prevented the related substances formation in the RG503H-octreotide system. Acetic acid and stearic acid were less efficient than lactic and glycolic acids in reducing the related substances formation in the RG503H-octreotide mixture.

In the experiment in which RG503H and octreotide in DCM/methanol incubated for 24 and 48 hour, added lactic acid and continued incubation for another 24 hours. The drug was extracted by the usual procedure. By this process lactic acid did not have any effect in reducing the related substances as these were already produced in the system prior to the incorporation of lactic acid. This shows that the presence of lactic acid initially in the dispersed phase prevented the amount of related substances, however later addition will not convert the related substances to the native drug. RG503 showed very high related substances level after 48 hour incubation. Polylactic acids, both PLA iv 0.11 and R203H and also PLGA 85:15 showed very little related substances even lesser than the control. Presence of triethylamine produced some impurities, however did not show similarity to related substance by retention time. TEA with RG503H produced huge amount of related substances with RG503H, and to a lesser extent with PLA iv 0.11. Thus, it has been demonstrated that the addition of acids initially to the dispersed phase reduces the amount of related substances. TABLE 27 Screening Study to Evaluate the Conditions for Octreotide Related substances Formation # Code Composition Note 1 Control Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 2 Control + LA Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + 85% Lactic acid (10 μL) 3 RG503H RG503H (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 4 RG503H + LA RG503H (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + 85% Lactic acid (10 μL) 5 RG503H + AA RG503H (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Glacial Acetic acid (10 μL) 6 RG503H + GA RG503H (20 mg) + Octreotide II (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Glycolic acid (10 mg) 7 RG503H + SA RG503H (20 mg) ++ Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Stearic acid (10 mg) 8 SA Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Stearic acid (10 mg) 9 RG503H − 40 + RG503H (20 mg) + Octreotide III LA + 40 (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + 85% Lactic acid (10 μL) 10 RG503 RG503 (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 11 PLA 0.11 PLA IV 0.11 (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 12 PLA 0.11 + TEA PLA IV 0.11 (20 mg) + Octreotide IV (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Triethylamine (40 μL) 13 85:15 PLGA PLGA 85:15 (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 14 R203H R203H (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 15 RG503H + TEA RG503H (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Triethylamine (10 μL) 16 TEA Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) + Triethylamine (10 μL) 17 Polycarbonate Polycarbonate (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) 18 Polysulfone Polysulfone (20 mg) + Octreotide (1.5 mg) + DCM (0.5 mL) + MeOH (0.1 mL) Note: II: GA was only partially soluble in the dispersed phase even at 40° C. III: To the extract prepared similar to #3, added 10 μL 85% lactic acid and incubated further at 40 C. for 24 hours. IV: Four times the amount in #16 and #17, since the acid end group from the polymer is large and will neutralize some TEA.

11. Octreotide Related Peptide Formation During In Vivo Incubation

The microspheres tested were prepared using RG503H (GJ091001), 8515DL1AP (GJ031401) and 100DLIAP (GJ012401). Blank microspheres without octreotide in the study were used as controls. The properties of the microspheres were as shown in Table 28 below. TABLE 28 Properties of the microspheres used for in vivo incubation GC091001 GJ031401 GJ012401 Polymer RG503H 8515DL1AP 100DL1AP Acid Number of the 7.4 13.6 21.5 polymer Target load  11%   11%  10% Method of making O/W process O/W process O/W process the MS Drug Load 8.5% 10.2% 8.5%

These microspheres were injected into rats subcutaneously and recovered at appropriate time. In this working example, 100 to 250 mg microspheres were suspended in 0.3 to 0.5 mL diluent consisting 6% mannitol, 0.5% carboxymethylcellulose and 0.1% Tween-80 in water. The suspension was injected to the subcutaneous region of the rats, at the site marked with a permanent marker. At appropriate time point, the rats were sacrificed, and the microspheres from the injection sites were excised and freeze-dried. Subsequently, the particles were dissolved in a mixture of 2 mL dimethylsulfoxide and 2 mL DCM, and extracted by adding 6 mL 0.1 M acetate buffer pH 4.0. The extracts were assayed by HPLC for the pure drug and related substance, and confirmed by mass spectrophotometer. Control (blank microsphere) did not show any peak by HPLC.

The levels of impurities (octreotide polymer fragment adducts) found in the microspheres, recovered from the rat tissue, were as shown in Table 29 below. TABLE 29 Impurities (Related Substance) (% impurity) from the microspheres after in vivo incubation Days GC091001 GJ031401 GJ012401 14 30.1 12.5 8.6 22 46.2 17.1 7.4 30 52.9 21.7 10.0 41 52.9 24.1 12.6

Separately, microspheres prepared from very similar polymers, however prepared by O/O process, were also studied. This set also includes the commercially available Sandostatin LAR, and control microspheres prepared from PLA without drug. The properties of the microspheres are as shown in Table 30 below. TABLE 30 Properties of the microspheres used for in vivo incubation Sandostain FR072402 FR062602 FR071002 LAR Polymer RG503H 8515DL1AP 100DLCO4 PLGA50:50- (Another name Glu of 100DL1AP) Acid Number 7.4 13.6 25.3 Not known of the polymer Target load 11%   8%  11% Not known Method of O/O O/O O/O Not known making the MS Drug Load 10% 7.4% 9.2% Approx. 5%

These microspheres were injected in to rat tissue and recovered on day 14, 22, 32 and 40. Shown in Table 31 below are the impurity profiles, The impurities are the Octreotide adducts with the polymer fragments as evidenced by HPLC and Mass spec. TABLE 31 Impurities (Related substance) from the microspheres after in vivo incubation (% impurity) Day FR072402 FR062602 FR071002 Sandostatin LAR 14 15.5 8.8 4.6 36.3 22 26.0 16.1 7.8 40.4 32 39.8 22.5 13.0 55.1 40 49.7 24.8 11.8 55.3

12. Octreotide Related Peptide Formation During In Vitro Incubation

For this working example, about 100 mg of octreotide microsphere was weighed into a 12-20 mL screw capped vial and added the release media. The release media were isotonic phosphate buffer, pH 7.4, 7.0 or 6. The contents were placed in a 37° C. shaking water bath. At each time point, the supernatant free from microsphere was carefully removed for HPLC analysis, and the entire media was replaced with fresh media. The cumulative release of octreotide and related substance was plotted against time. As the incubation proceeded, the related substance released from the microsphere also increased. However, microspheres with 85% PLA and 100% PLA produced less amount of related substance. The difference was more pronounced at low pH.

Shown in FIG. 13A is percent related substance formation during in-vitro release of octreotide from PLGA 75:25 (MG090899), 50:50 (GJ033100 and GJ051600) 85:15 (GJ021501), and PLA microspheres at 37° C. in an isotonic phosphate buffer. PLGA50:50 produced hydrophobic impurities at a faster rate. PLA produced the impurities at a slower rate. PLGA with 85% and 75% lactide content produced impurities at a rate higher than PLA and lower than PLGA 50:50. These release studies were performed in pH 7.4 buffer and the release media was replaced frequently. A separate release study was performed on PLGA 50:50, PLGA 85:15 and PLA based microspheres at pH 7. The related substance formation in these microspheres were compared. At pH 7, there was a steady increase in related substance similar to the pattern observed at pH 7.4, however, less in magnitude. Shown in FIG. 13B is a comparison of the related substance formation during in-vitro release of octreotide from these microspheres at 37° C. in an isotonic phosphate buffer at pH 7. Shown in FIG. 13C is a comparison of the related substance formation during in-vitro release of octreotide from PLGA 50:50, PLGA 85:15 and PLA microspheres at 37° C. in an isotonic phosphate buffer at pH 6. At pH 6, there was a considerable difference among the 50:50 PLGA and the PLGA with higher lactide content. The related substance formation reduced considerably for the 85:15PLGA and PLA microspheres, while the PLGA 50:50 PLGA based microspheres still showed related substance.

13. Hydrophobic Related Substances Formation By Drug Extraction Procedure

The drug extraction procedure did not cause the hydrophobic related substances. To show this, approximately 1 mg octreotide acetate was mixed with 10 mg polymer (R203H, R202H, PLA 0.11, PLGA90:10 (iv 0.11), PLGA 85:15DL2A, PLGA 75:25H (BI), RG504H and RG503H). To the mixture, added 2 mL acetonitrile/water (9:1) and dissolved the entire content. Clear solution was obtained in all cases. To that added 8 mL acetate buffer (0.1 M, pH 4.0) and mixed well for 10 minutes. The turbid solution was filtered through 045 micron PTFE syringe filter and assayed by HPLC. Controls without drug and without polymer were also included in the study. There was no hydrophobic related substances found in the extract. The drug recovery was slightly above 100% (actual values were 101-103%) which shows that there was no loss of drug and also proves that the drug recovery method results in accurate value (data not shown).

14. Storage Stability

To demonstrate storage stability of Octreotide Containing PLGA microspheres, microsphere batches were prepared with both 85:15PLGA and 50:50 PLGA and stored under different temperature conditions.

The properties of the polymer, composition of the dispersed phase and the properties of the microsphere are provided in Table-32. TABLE 32 Properties of the polymer, polymer solution and microspheres GC100903 GC111703 Polymer Co-monomer 85% Lactide 50% Lactide properties composition 15% Glycolide 50% Glycolide Mw of the polymer 10 kDa 30 kDa Acid Number 17.2 7.4 Composition Polymer in DP, % 33.88 16.47 of Dispersed Phase Octreotide Acetate 3.76 1.24 in DP, % Methylene chloride 53.01 70.14 in DP, % Methanol in DP, % 5.33 7.02 Glacial acetic 4.02 5.08 acid in DP, % Target drug in 10 7 microsphere, % Properties of Drug load in the 7.82 5.65 the microsphere, % Microsphere Encapsulation Efficiency, % % Impurity (Total) None 3.4 detected Bulk Density, g/mL 0.61 0.72 Particle Size, Vol. dist 10% under 4.17 2.82 25% under 10.3 11.94 50% under 23.9 26.32 75% under 37.8 38.99 90% under 46.8 49.04

GC100903 microsphere prepared from 85:15 PLGA having acid number 17.2 did not show any impurity, while GC111703 prepared from 50:50 PLGA having acid number 7.4 showed 3.4% initial impurity, despite the lower target load. These microspheres were subjected to storage stability and compared to that of the commercial octreotide microsphere, Sandostatin LAR. Microspheres were stored at −20° C., 2-8° C. (refrigerated), 25° C. and at 40° C. After three month storage the batch GC100903 showed better storage stability compared to GC111703 and Sandostatin LAR. The storage stability data is shown in Table 33. TABLE 33 Percentage Impurities (Related Substances) in Octreotide Containing Microspheres Upon Storage Storage Storage Sandostatin duration Condition GC100903 GC111703 LAR Initial N.A None 3.4% 6.6% detected 3 Months −20° C.   None 3.3% 6.2% detected 2-8° C.  None 3.3% 6.1% detected 25° C. None 6.9% 8.4% detected 40° C. 1.8% 17.2%  23.3%  As shown herein, the octreotide microspheres prepared from a polymer solution containing 85% lactide can be stored at room temperature with undetectable peptide related substances, whereas the commercially available octreotide microsphere, Sandostatin LAR, requires at least refrigeration for storage.

15. Efficacy of Octreotide Microspheres Having No Detectable Impurities

Octreotide acetate containing polymer solutions were prepared using several PLGA85:15 polymers (GC091903, GC091203, GC091503, GC091703 and GC091603). The acid number of the polymers ranged from 14 to 18. Microspheres were prepared by dispersing the dispersed phase in the continuous phase (0.35% polyvinyl alcohol solution) by the continuous flow process described in U.S. Pat. Nos. 5,945,126 and 6,270,802. Properties of the polymer, composition of various components in the dispersed phase, and the properties of the microspheres were as shown in Table-34 below.

The microspheres so prepared were recovered and formulated in a diluent, which is a solution of carboxymethylcellulose, mannitol and tween-80. Each vial had 5 mg octreotide acetate. The microspheres had drug encapsulation efficiency ranging from 76 to 81% and there were no detectable impurities (related substances) in the microspheres. The microsphere suspensions in diluent were then freeze-dried to achieve the formulation that is suitable for the in-vivo evaluation. TABLE 34 Properties of 85:15 PLGA Polymers, Dispersed Phase Formulations and the Properties of the Microspheres Polymer Lot GC091903 GC091203 GC091503 GC091703 GC091603 Polymer Polymer Lot# 02-012-105 03-001-085 03-001-097 03-001-105 03-001-114 Properties Co-monomer 85% Lactide 85% Lactide 85% Lactide 85% Lactide 85% Lactide composition & 15% & 15% & 15% & 15% & 15% Glycolide Glycolide Glycolide Glycolide Glycolide Acid Number of the polymer 14.8 17.5 17.8 17.1 17.2 Mw of the polymer 13395 11546 10307 10507 10961 Dispersed Polymer in DP, % 29.7 29.7 29.7 29.7 29.7 Phase Octreotide Acetate in DP, % 3.3 3.3 3.3 3.3 3.3 Composition Methylene chloride in DP, % 57.3 57.3 57.3 57.3 57.3 Methanol in DP, % 5.7 5.7 5.7 5.7 5.7 Glacial acetic acid in DP, % 4.0 4.0 4.0 4.0 4.0 Target drug in microsphere, % 10% 10% 10% 10% 10% Microsphere Drug load in the microsphere, % 8.1 7.7 7.8 7.6 7.7 Properties Encapsulation Efficiency, % 81 77 78 76 77 % Impurity (Total) <0.1 <0.1 <0.1 <0.1 <0.1 Bulk Density, g/mL 0.70 0.70 0.61 0.65 0.74 Particle Size, Vol. dist 10% under 2.19 2.76 3.16 2.59 2.80 25% under 9.61 10.0 13.3 8.72 10.6 50% under 20.8 23.1 25.4 21.6 24.9 75% under 30.2 33.3 35.0 30.8 34.4 90% under 37.8 41.5 43.6 38.3 42.1

Freeze-dried dosage forms were then reconstituted with water and the resulting microsphere suspensions were injected s.c. in rats; five rats for each microsphere formulation. Blood samples were withdrawn at appropriate intervals and the growth rate of the rats were also followed. Shown in FIG. 14 is data on the serum octreotide level in rats injected with octreotide microspheres (microsphere lots GC091903, GC091203, GC091503, GC091703 and GC091603) containing no detectable impurities. The control rats received only diluent (without microsphere) and the octreotide concentration found in the serum is zero or negligible. Shown in FIG. 15 is data on the percentage increase in body weight compared to the time when they first received the octreotide microspheres (microsphere lots GC091203, GC091503, GC091603, GC091703 and GC091903) containing no detectable impurities. Control indicates body of weight of rats that received only diluent. The reported values are the average from five rats.

The microspheres were one-month release formulations. It is known in the art that octreotide in serum controls the growth hormone (GH) and insulin-like growth factor-1 (IGF-1) in acromegaly patients (McKeage et al., 2003, Octreotide Long-Acting Release (LAR)—A Review of its Use in the Management of Acromegaly, Drugs 63 (22): 2473-2499. It is shown, by way this example herein that impurity free octreotide microspheres of the present invention is effective in controlling or reducing the growth rate of the rats.

G. Leuprolide Microspheres

1. Leuprolide PLGA Microspheres

Three microsphere batches were prepared with PLGA 50:50 from a clear dispersed phase by the same procedure described above for octreotide microspheres. See Table 35 below. TABLE 35 Leuprolide Microsphere with PLGA50:50 PLGA Acid Target Drug Batch used Number Load Load % Impurity TV061297 RG503H 7.4   18% 14.0%  3.46 BT073096 RG503H 7.4 12.5% 9.5% 2.32 BT103196 RG502H 29.3 12.5% 9.4% 0.21

2. Effect of Molecular Weight (or Effect of Acid Number):

Another batch, BT103196 was prepared with low molecular weight polymer RG502H. The target load was 12.5% and the actual load was 9.4%. The percentage impurity, as polymer-drug adduct is only 0.21%.

3. Effect of Target Load:

Leuprolide acetate microsphere was prepared with RG503H at two target loads. Batch TV061297 was prepared with the target load of 18% and resulted in microspheres with 14% drug load. The resultant microspheres had 3.46% impurities as drug polymer adduct. Batch BT073096 was prepared with the same RG503H polymer at 12.5% target load. The resultant microspheres had 9.5% drug load and 2.32% impurities.

Shown in FIG. 16 is the HPLC chromatogram of the extract from a RG503H microsphere, TV061297. The structure of the impurities marked in FIG. 16 were identified by HPLC-MS, and shown below: Peak ID Structure 1 [5-OxoL-Prolyl]-[L-histidyl]-[L-tryptophyl]- [L-Seryl]-[L-Tyrosyl]-[D-Leucyl]-[L- Leucyl]-L-[L-arginyl]-[N-ethylprolinamide] (Leuprolide acetate) 2 [5-OxoL-Prolyl]-[L-histidyl]-[L-tryptophyl]- [L-Seryl]-[L-Tyrosyl]-[D-Leucyl]-[L- Leucyl]-L-[L-arginyl-GLY]-[N-ethylprolinamide] 3 [5-OxoL-Prolyl]-[L-histidyl]-[L-tryptophyl]- [L-Seryl]-[L-Tyrosyl]-[D-Leucyl]-[L- Leucyl]-L-[L-arginyl-GLY-GLY]-[N-ethylprolinamide] 4 [5-OxoL-Prolyl]-[L-histidyl]-[L-tryptophyl]- [L-Seryl]-[L-Tyrosyl]-[D-Leucyl]-[L- Leucyl]-L-[L-arginyl-GLY-LAC]-[N-ethylprolinamide] 5 [5-OxoL-Prolyl]-[L-histidyl]-[L-tryptophyl]- [L-Seryl]-[L-Tyrosyl]-[D-Leucyl]-[L- Leucyl]-L-[L-arginyl-LAC-LAC]-[N-ethylprolinamide]

4. Leuprolide PLA Microspheres

Three leuprolide microsphere batches were prepared with polylactide. See Table 36 below. TABLE 36 Leuprolide Microspheres with PLA Acid Target Actual % Total Batch Polymer No. Load, % Load, % Impurity GJ110899 PLA0.22 9.6 15.5 10.2% 0.67 GJ110299 PLA, IV 0.11 19.9 15.5% 11.0% 0.29 GJ111999 PLA, IV 0.11 19.9 15.0% 10.6% 0.27

As shown in the Table 36, leuprolide microspheres with polylactide produced less impurities relative to the PLGA microspheres. Also, it was shown that lower the molecular weight (higher acid number), lower the impurity.

5. Chemical Castration in Prostate Cancer Patients Treated with Leuprolide PLA Microspheres

Leuprolide containing microspheres were prepared at 480 g scale using a dispersed phase containing glacial acetic acid. The dispersed phase composition is shown in Table-37. TABLE 37 Composition of the Dispersed Phase Amount, g % Composition Polylactide 401 25.0 Dichloromethane 852 53.0 Leuprolide acetate 79.1 4.92 Glacial Acetic acid 6.7 0.42 Methanol 268 16.7

Microspheres were made from the dispersed phase by the continuous flow process under aseptic conditions using the procedure described in the U.S. Pat. Nos. 5,945,126 and 6,270,802. The microspheres so prepared were formulated in a diluent, which was a sterile solution of carboxymethylcellulose, mannitol, and tween-80. The microsphere suspension in the diluent was then filled into vials to have 22.5 mg leuprolide acetate per vial (plus the overage to accommodate the transfer loss) and freeze-dried. The properties of the finished dosage form is shown in the Table-38 below. TABLE 38 Properties of the Microsphere Leuprolide acetate content per vial* 23.2 mg Leuprolide load in the microsphere 13.4% Particle size, Vol. Distribution 10% under  3 micron 25% under 12 micron 50% under 25 micron 75% under 36 micron 90% under 45 micron pH upon reconstitution 6.9 Moisture content, % 0.1% Accelerated drug release  5 Hours 20% drug released 24 Hours 50% drug released 48 Hours 73% drug released 72 Hours 86% drug released *Filled with ≈10% overage and Intent to deliver 22.5 mg leuprolide acetate.

A comparison of the molecular weight of the polymer used for the microsphere preparation and the molecular weight of the polymer in the microsphere (data presented in Table-39 below) showed that the Mw of the polymer did not change upon microsphere formation. TABLE 39 Molecular weight (Mw) of the raw polymer and the microsphere Mw % Change in Mw Raw polymer 14321 N.A MS Batch# 0H 14420 +0.7

The microspheres were injected once in every three months to chemically castrate and maintain prostate cancer patients. In patients with prostate cancer, achieving serum testosterone levels of less than or equal to 0.5 ng/ml (chemical castration level) is a desired pharmacological indicator of therapeutic action. Thus, physiologically, the patients that received the leuprolide microsphere should have their serum testosterone level reduced to or below 0.5 ng/mL by four weeks or earlier and should maintain that castrate level for the entire duration of the therapy. In all, forty prostate cancer patients received the microsphere injections (intramuscular injections). Twelve patients were monitored for the serum leuprolide to follow the pharmacokinetics and all the patients were monitored for serum testosterone. FIG. 17 shows the serum leuprolide level and their testosterone level. Chemical castration was achieved within 28 days in 39 patients out of 40. After achieving castration, all the patients maintained castration for the entire treatment period. The second injection of the formulation did not produce testosterone surge and maintained the low testosterone level.

H. Orntide Microspheres

Orntide (Ac-D-2Nal-D-4 Cpa-D-3 Pal-Ser-Lys(Pic)-D-Orn(6-Aminonicotinoyl)-Leu-Ilys-Pro-D-Ala-NH₂) containing microspheres with several polymers were made. One impurity has been found in large amount while preparing the orntide microspheres with PLGA5050. This compound eluted just before orntide and identified as Orntide-glycolide adduct through serine. This peak eluted before orntide in HPLC because, orntide is comparatively hydrophobic. Few other impurities were also observed after orntide, which were not identified, and assumed that they are adducts with larger fragments from PLGA. As seen with the octreotide and leuprolide microspheres above, PLGA with higher lactide content produced less impurity. Orntide microspherers prepared with PLA did not show individual impurity large enough to report. Following Table 40 shows examples of Orntide microsphere with PLGA TABLE 40 Orntide microspheres with PLGA Sum of other % Acid Target Actual Orn-Gly impurities & No. Batch Polymer Lactide No. Load Load adduct of impurities GJ022300 RG504H 50 5.9 21% 14.2% 1.87% 1.43% (Five) GJ022900 RG503H 50 7.4 22% 15.2% 1.64% 1.38 (Four) GJ022400 7525DL3A 75 6.7 21% 14.0% 0.52% 0.57 (Two or Three) I. WOC4D Microspheres

WOC4D, a structure of which is shown below, is another somastostatin analog like octreotide.

WOC4D microspheres with several polymers were made. WOC4D microsphere also showed a similar behavior as seen with octreotide microspheres. The level of adduct formation, however, is much less. The following Table 41 shows examples of WOC4D microsphere with PLGA. TABLE 41 WOC4D microspheres with PLGA Target Actual Sum of Batch Polymer % Lactide Acid No. Load Load Impurities GJ062199 RG503H 50 7.4 13% 7.9 1.46 GJ070199 RG504H 50 5.9 13% 8.4 1.74 GJ050499 RG503 50 0.5 11.1%   8.2 1.97 MG052500 8515DL2A 85 19.2 15% 13.4 0.22 MG050200 PLA iv 0.11 100 19.9  9% 8.2 0 J. Orntide Containing Formulation and Prevention of its Gelling

1. Orntide Solubility With and Without an Acid Additive in Dispersed Phase

Solubility of orntide in dichloromethane (DCM) and methanol was evaluated.

Orntide received from various sources showed insolubility and gelling characteristics in DCM-methanol mixture. In general, it was found that the solution was not very clear and had a tendency to gel quickly. Glacial acetic acid helped to form a clear solution. However, the amount of glacial acetic acid required to achieve the solubility varied with manufacturer and with Lot#. Solubility of three orntide raw material from various sources were also compared by the solubility test in presence of glacial acetic acid. To 84 mg orntide acetate, added 100 mg glacial acetic acid initially and added 130 mg methanol. After mixing these components well forming a clear solution, 1.28 g methylene chloride was added and warmed the mixture to 40° C. for about 5 minutes to form a clear solution. Table-42 provides the comparative account of the gellation. In all threes cases, acid was added first to orntide sample and the solution formed after adding all additives were clear. However, PPL-ORN-9902 turned into gel within 30 minutes. TABLE 42 Solubility Comparison of Orntide Acetate PPL-ORN-9901 PPL-ORN-9902 MG#401 Polypeptide Lab Polypeptide Lab California Peptide Lab Clear solution, Gelled within 30 min and Clear solution. Hazy and stable for more turned into White pasty tendency to gel after one than one hour. mass. hour

Adding glacial acetic acid and warming the solution improved the solubility However, the solution showed some gelling, depending upon the source and Lot#. Dispersed phases were prepared with various polymers to prepare microspheres containing PPL-ORN-9902 as shown in Table-43. The DP started gelling, and heating reversed the gelation but went back to gel after the DP cooled down to room temperature and was stored for about 10 minutes. TABLE 43 Preparation Parameter of DP Polymer GJ013100 BT020800 GJ011900 7525DL3A GJ020400 BT020300 8515DL2A PLA iv 0.11 Alkermes RG503H BI RG504H BI Alkermes BPI, Lot# 99115 Lot# 97-12-113 Lot#281334 Lot#34020 Lot# 96-11-178 Amount of Polymer, g 3.5 2.46 1.56 2.34 2.37 Amount of Orntide, g 0.5 0.54 0.44 0.66 0.63 Amount of DCM, g 7.5 12.0 7.0 12.0 5.0 Amount of MeOH, g 0 0.6 0.7 1.2 0.5 Amount of Acetic acid, g 2.50 2.2 1.4 2.2 1.2 % Acetic acid in DP 17.9 12.4 21 12 12 Properties of DP after Hazy, gelling Hazy. Clarity Clear after Clear after Clear after heating to 60 C. improved heating to heating to heating to with MeOH 60 C. 60 C. 60 C.

Up to 22% glacial acetic acid was required for the DP to form a clear and filterable DP solution. DP with such high quantity of acetic acid may not form desirable microspheres by O/W process, if the molecular weight of the polymer is lower than 10,000 (data not shown).

Other acids having low pKa values such as HCl, glycolic acid, and Lactic acid (85% solution in water) also helped to achieve the solubility and stability of DP. However, anhydrous acids are preferred to avoid phase separation caused by the water. HCl and lactic acid are available with water. Hence, these acids in DP could cause phase separation. Lactic acid with lower water content did not cause phase separation and prevented gelation. Lactic acid with 85% water (commercially available) prevented gelation, however phase separation was observed in the DP. The composition of tested DP contained, 0.22 g orntide, (Lot# PPL-ORN-9902), 0.6 g methanol, 0.78 g RG503H, 4.0 g DCM, and appropriate amount of acid as shown in Table-44. The stability was followed for a day. TABLE 44 Solubility Performance of Orntide DP Containing Acids with low pKa Acid Type & % % Acid Composition in DP in DP Observation Conc. Hydrochloric   5% Two clear phases, upon mixing acid turns hazy due to two phase mixing. No gelling upon storage. Conc. Hydrochloric 2.5% Two clear phases, upon mixing acid turns hazy due to two phase mixing. No gelling upon storage. Conc. Hydrochloric    2.5% + Two clear phases, upon mixing acid and 85% Lactic 2.5% turns hazy due to two phase Acid mixing. No gelling upon storage 85% Lactic acid   5% Hazy even after warming. Gelled overnight 85% Lactic acid  11% Two phases. No gelling. Lactic acid: 11%  11% Clear and stable solution. (Mol. Sieves treated)* *Molectular sieves reduced the water content in 85% lactic acid from 15% to approx. 7%.

2. Improving the Solubility of Raw Orntide in DP from Non-Aqueous Solvents

In an attempt to minimize the amount of acid to be used to dissolve orntide in organic solvents, an attempt was made to re-freeze dry orntide with appropriate solvent system. Two organic solvents which could be freeze dried under normal freeze drying cycle are, tert-butanol (TBA) and cyclohexane. In this study 40 mg/mL solution of orntide was made in TBA-Water mixture. To a set of sample, glacial acetic acid was also added. The solution was then freeze dried using the cycle below: Freezing: −50° C. for 2 hours Drying: Ramp from −50° C. to 10° C. over 20 hour period. Ramp from 10° C. to 25° C. over 20 hour period Terminal drying at 25° C. for approx. 10 hours.

The list of solutions underwent the freeze drying are shown in Table-45. TABLE 45 Orntide solutions in TBA water for freeze drying to improve solubility % TBA/% Other Orntide (100 mg) Water additives Conc. Code Cal. Peptide, 23/74 3% 40 mg/mL H MG0401 Acetic acid PPL-ORN-9902 23/74 3% 40 mg/mL I Acetic acid PPL-ORN-9902- 23/74 3% 40 mg/mL J EDTA Cleaned* Acetic acid PPL-ORN-9902 76/24 No 40 mg/mL K PPL-ORN-9902 44/56 No 100 mg/mL  L PPL-ORN-9902 34/66 No 50 mg/mL M PPL-ORN-9902 34/66 No 100 mg/mL  N *Orntide treated with EDTA solution to remove ions.

Freeze-dried orntide went through a dispersed phase formation and gellation study, with the following DP composition.

-   Orntide: 84 mg -   Methanol: 150 mg -   Glacial acetic acid: 200 mg -   DCM: 1280 mg -   R202H: 450 mg.

Thus, the DP contained 9.2% acid in the formulation. Freeze dried orntide from “M” produced clear DP which was stable for a week. Other formulations showed improved solubility compared to the original material, but not as good as sample “M”. As per the request of Oakwood Labs, Polypeptide Lab re-freeze dried the peptide in TBA-Water mixture and sent the material. Several microsphere batches were produced with the re-freeze dried orntide with TBA. Table-45 shows the preparation parameters, which showed that 11% acetic acid in the DP formulation is sufficient to form stable DP. Table-46 shows the properties of the microspheres. TABLE 45 Preparation parameters of Orntide Microspherere Batches Preparation Parameters GJ081000 GJ081500 GJ082100 GJ082400* Polymer RG503H RG503H RG503H RG503H Source/Lot# BI 281334 BI 281334 BI 281334 BI 281334 Batch Size 1.0 g 1.0 g 1.0 5.0 Target load 21 18 21 21 Polymer Conc. 16.5 16.5 16.5 15.3 in DCM MeOH/DCM 0.15 0.15 0.15 0.15 Acetic acid in DP 11% 11% 16%** 11% Silverson RPM 5000 4000 4000 4000 CP/DCM 200 193 200 182 CP: Conc. Of 0.1 M, 7.4 0.1 M, 7.4 0.1 M, 7.4 0.1 M, 7.4 PB and pH *Used in-line mixer **To check the influence of higher acetic acid in DP on testosterone suppression in rat

GJ081000 had 21% target load and GJ081500 had 18% target load. Drug incorporation efficiency was not affected while targeting 21% drug load. GJ082400 also had 21% target load, however prepared using an in-line mixer. Drug incorporation efficiency was not affected, however slightly larger amount of non-spherical particles were found in the product. GJ082100 also had 21% target load, however the DP contained 16% acetic acid. TABLE 46 Properties of Orntide Microspheres Properties GJ081000 GJ081500 GJ082100 GJ082400 Drug Load, % 17.5 13.58 16.24 17.74 Drug incorp. 83% 75% 77% 84% Efficiency Drug in CP Initial 26.27 26.12 19.21 32.02 EV-0 min 20.52 24.64 12.84 17.85 EV-60 min 12.34 18.95 12.34 17.50 Final 13.81 16.04 25.21 17.14 Mass balance 97 91 102 101 Particle size 10% Under 1.29 1.32 1.79 2.27 25% Under 3.09 3.20 5.51 6.24 50% Under 8.25 9.13 12.81 14.56 90% Under 29.61 27.5 35.75 31.33

Two microsphere batches, GJ082100 and GJ082400, were formulated at 3 mg/vial orntide and freeze dried. The formulated microspheres were administered to rats at 3 mg/Kg by sc injection.

FIGS. 18 and 19 show the testosterone suppression for the rats that received one of the two batches, i.e., GJ082100 or GJ082400.

3. Order of Adding Acid Additive, Orntide and Other Components to Form DP

Acetic acid required in the DP was added first to the orntide and orntide was soluble in that limited amount of acetic acid. Followed by that, methanol or/and a portion, preferably half of the DCM required in the formulation was added to the orntide solution in acetic acid. The remaining DCM was used to dissolve the PLGA or PLA. The viscous polymer solution and the orntide solution were mixed together to form the DP. This DP showed better filterability and stability against gellation than when the acid was added to the DP. Instead of adding portion of the DCM in the DP to the orntide solution in acid, methanol or combination of methanol and DCM could be added. The formulation tested had the composition, 0.984 g RG503H, 0.22 g orntide, 0.85 g glacial acetic acid, 5.0 g DCM and 0.74 g Methanol. The effect of order of the addition of the components were checked. To form a clear solution, the acetic acid should be added first forming a clear solution. Then by adding half of DCM (2.5 g) or the methanol, it formed into a less viscous and clear solution. Then, the solution could be mixed with the polymer solution. The orntide solution in acetic acid could also be admixed with the polymer solution directly.

4. Suppression of Testosterone Levels in a Mammal by Orntide Containing Microspheres Made of PLGA or PLA Polymer Matrix

Orntide microspheres were prepared using the appropriate PLGA or PLA to achieve release for nine months to one year. The preparation parameters and properties of the orntide microspheres are shown in Table-47. The dispersed phase was prepared as described above using the freeze-dried orntide acetate. Polyvinyl alcohol solution buffered to pH>7.5 was used as the continuous phase. The microspheres were prepared using the procedure described in the U.S. Pat. No. 5,945,126 using in-line mixer at 4000 RPM, and the subsequent solvent removal and washing were performed as described in the U.S. Pat. No. 6,270,802. TABLE 47 Preparation Parameter and Properties of the Orntide Microspheres GC102301 GC010402 DP Polymer 85:15 PLGA PLA Composition (Mw 81 kDa) (Mw 30 kDa) Polymer conc., % 9.6 13.5 Dichloromethane, % 70.5 64.8 Orntide conc., % 2.2 2.4 Glacial acetic 10.0 10.9 acid, % Methanol, % 7.7 8.4 Microsphere Drug Load, % 11.0 12.2 Properties Encapsulation 61 81 Efficiency, % Particle Size (volume distribution) 10% under  1.9 μm  1.9 μm 25% under  4.9 μm  5.1 μm 50% under 15.1 μm 13.7 μm 90% under 36.5 μm 21.8 μm

The microspheres so obtained were suspended in a diluent containing carboxymethyl cellulose, tween-80 and mannitol and freeze dried in vials.

Rats were dosed (subcutaneously) at 27 mg orntide acetate per kilogram body weight, assuming that the formulation will release the drug for about 12 months duration. It was established previously that 2.25 mg per month is effective dose for chemical castration (testosterone below 0.5 ng/mL) of rats if provided as sustained release formulation. Six rats received each microsphere formulation.

FIG. 20 shows the serum orntide level and the serum testosterone level in rats that received GC102301 and FIG. 21 shows the serum testosterone level in rats that received GC010402. The orntide microspheres were effective in rapidly suppressing testosterone to castration levels and maintaining at those levels for extended periods. The GC102301 was effective for 9 months and GC010402 was effective for little over 12 months.

K. Leuprolide Containing Formulation and Prevention of its Gelling

While making leuprolide microsphere which has an step of dissolving leuprolide in methanol at 0.24 g/g, there was a gellation/precipitation of leuprolide. The precipitated/gelled leuprolide could not be turned back in to solution even by adding huge amount of methanol. Previous experience shows that 0.14 g/g solution of leuprolide in methanol is stable and clear for at least a day.

Initially, leuprolide dissolved easily in methanol, forming a clear solution at 0.24 g/g concentration. However, while it was approaching towards complete solubility, the leuprolide precipitated out of the solution rapidly, become a thick, white gel. A brief investigation study was performed on leuprolide solution in methanol and in dispersed phase.

This study was performed to compare the stability of leuprolide/methanol solution and the stability of the DP. Table-48 compares the stability of DP. TABLE 48 Stability of Leuprolide Solution in Methanol and in DP Leuprolide in DP (Leup, MeOH, Polymer & DCM) Leuprolide Solution in Methanol Type Supplier/Lot# Conc. (g/g) Stability Polymer of DP* Stability Bachem, 0.14 Stable and clear RG503H 30 Day Stable for 5 days FLEUP9901 for 4 days. Bachem, 0.14 Stable and clear RG503H 30 Day Stable for 2 days FLEUP9805 for 2 days Bachem 0.24 Hazy after 30 R202H 90 Day Hazy after 30 min, FLEUP9805 min gelled on the same day Peninsula, 769A, 0.14 Stable and clear RG503H 30 day Clear for 2 days purified for 3 days (viscosity higher (Lot#036973) than Bachem Leup) Peninsula, 769A, 0.24 Stable and clear R202H 90 Day Stable for 30 purified for 40 min minutes, turned hazy (Lot#036973) and viscous after 30 min Bachem 0.24 Cloudy after 2 FLEUP9901 hours Trace of glacial 0.24 Clear solution, acetic acid and stable for >7 days Bachem Leup9901 *Note: 30 Day DP is obtained by mixing 0.612 g of 0.14 g/g leuprolide/methanol solution and 2.2 g of 0.18 g/g RG503H/DCM solution. 90 Day DP is obtained by mixing 1.05 g of 0.24 g/g leuprolide/methanol solution and 3.95 g of 0.32 g/g R202H/DCM solution.

The addition of acetic acid to the solution proved to provide excellent stability for Bachem leuprolide against gelling/precipitation of leuprolide from its methanol solution as well as in DP. It is necessary to find the effective amount of acetic acid required to keep the DP stable for an extended period of time. The DP formulation is very similar to the 90 day leuprolide formulation. Solutions of both Bachem and Peninsula leuprolide were prepared with acetic acid to evaluate the stability. Table-49 shows the result. TABLE 49 Acetic acid and DP Stability Leuprolide Methanol solution* Dispersed phase** Composition Performance Performance Bachem FLEUP9805 Stable for 5 days Stable for one week (0.4 g) + 75 mg Glacial acetic acid + Methanol (1.27 g) Bachem FLEUP9805 Stable for 5-6 hours Stable for 5-6 hours (0.4 g) + 7.5 mg Glacial acetic acid + Methanol (1.27 g) Peninsula purified, 769-A Stable for 3 days Stable for 4 days (0.4 g) + 75 mg Glacial acetic acid + Methanol (1.27 g) *It is a 0.24 g/g solution **90 Day DP composition with polymer, R202H

Table-50 shows the minimum acetic acid composition required in the DP for stable solution. TABLE 50 Suggested Composition for the 90 Day DP formulation % Amt in Methanol % Amt. Component Amount (g) solution (wt) In DP Leuprolide acetate 4 g 24.3% 5.4 Acetic acid 0.075 g  0.4% 0.1 Methanol 12.4 g 75.3% 16.8 R202H 18.4 N.A. 24.9 DCM 39.0 52.8

Several microsphere batches at approx. 400 g and approx. 800 g were prepared and tested in rats, dogs and human. The composition of the dispersed phase is shown in Table-10. TABLE 51 Composition of two batches produced under sterile condition for clinical study Approx. 400 g Approx. 800 g Batch scale batch scale batch Polymer R202H from BI R202H from BI Leuprolide source Bachem Bachem Amount of R202H 401 g 598 g Amount of Leuprolide 82 g 123 g acetate Amount of Glacial 7 g 10 g acetic acid Amount of methanol 268 g 390 g Amount of DCM 852 g 1250 g Microsphere produced at 400 g has been evaluated in human also, and found to castrate>95% men within a month and maintained castration for the tested period, three months.

All publications, patents and patent applications mentioned in this specification are indicative of the level of those skilled in the art to which this invention pertains. The contents of all the publications, patents and patent applications are incorporated herein by reference to the same extent as if each individual publication, patent or patent application was specifically and individually indicated to be incorporated by reference.

Although the foregoing invention has been described in some detail by way of illustration and example for purposes of clarity of understanding, it will be obvious that certain changes and modifications may be practiced within the scope of the appended claims. 

1. A sustained release formulation comprising: a biocompatible and biodegradable polymer, at least one nucleophilic substance capable of catalyzing ester bond cleavage and causing molecular weight reduction of the polymer, and an amount of an acid additive such that the polymer in the formulation is less susceptible to molecular weight reduction as compared to the formulation without the acid additive.
 2. The sustained release formulation of claim 1, wherein the polymer is a copolymer of poly(d,l-lactic acid) or poly(l-lactic acid) and poly(glycolic acid).
 3. The sustained release formulation of claim 1, wherein the nucleophilic substance is a peptide, or a drug having a nucleophilic group.
 4. The sustained release formulation of claim 3, wherein the nucleophilic substance is a peptide, ketotifen, thioridazine, risperidone, oxybutynin, olanzapine, naloxone and naltrexone, and pharmaceutically acceptable salts thereof.
 5. The sustained release formulation of claim 4, wherein the peptide is selected from the group consisting of octreotide, leuprolide, orntide and Woc4D.
 6. The sustained release formulation of claim 1, wherein the acid additive comprises one or more organic acids having a pKa of 5.0 or lower.
 7. The sustained release formulation of claim 6, wherein the acid additive is lactic acid, glycolic acid, acetic acid, glyceric acid, benzoic acid, propanoic acid, carboxy terminated oligomers of lactic acid, carboxy terminated oligomers of glycolic acid, carboxyl formulated or oligomers of lactides-co-glycolides, or a combination of these acids.
 8. The sustained release formulation of claim 6, wherein final amount of acid additive present is about 0.1% to 5%.
 9. The sustained release formulation of claim 6, wherein the amount of acid additive is about 2% to about 50% by weight of the polymer.
 10. The sustained release formulation of claim 6, wherein the amount of acid additive in the sustained release formulation is about 1.0% to about 10%.
 11. The sustained release formulation of claim 1, wherein the formulation is prepared at temperatures greater than 25° C.
 12. The sustained release formulation of claim 1, wherein the formulation is prepared at temperatures greater than 40° C.
 13. The sustained release formulation of claim 1, wherein the formulation contains a solvent that enhances the reactivity of nucleophilic substances.
 14. The sustained release formulation of claim 13, wherein the solvents are methanol, dimethylacrylamide, ethanol, dimethylsulfoxide, dimethylformamide or NMP or a combination thereof.
 15. A dispersed phase formulation comprising: a biocompatible and biodegradable polymer, at least one nucleophilic ingredient capable of catalyzing ester bond cleavage of the polymer and causing molecular weight reduction of the polymer, and an amount of an acid additive such that the polymer in the formulation is less susceptible to molecular weight reduction as compared to the formulation without the acid additive.
 16. The dispersed phase formulation of claim 15, wherein the polymer is a copolymer of poly(d,l-lactic acid) or poly(l-lactic acid) and poly(glycolic acid).
 17. The dispersed phase formulation of claim 15, wherein the nucleophilic ingredient is methanol or a peptide or an organic compound having a nucleophilic group.
 18. The dispersed phase formulation of claim 17, wherein the nucleophilic ingredient is a peptide, ketotifen, thioridazine, risperidone, oxybutynin, olanzapine, naloxone or naltrexone or pharmaceutically acceptable salts thereof.
 19. The dispersed phase formulation of claim 18, wherein the peptide is selected from the group consisting of octreotide, leuprolide, orntide and Woc4D.
 20. The dispersed phase formulation of claim 15, wherein the acid additive comprises one more organic acids having a pKa of 5.0 or lower.
 21. The dispersed phase formulation of claim 20, wherein the acid additive includes lactic acid, glycolic acid, glacial acetic acid, glyceric acid, benzoic acid, propanoic acid or carboxy terminated oligomers of lactic acid, carboxy terminated oligomers of glycolic acid, carboxyl formulated oligomers of lactides-co-glycolides, or a combination thereof.
 22. The dispersed phase formulation of claim 20, wherein the amount of acid additive is about 2% to about 50% by weight of the polymer.
 23. A method of preparing a sustained release formulation comprising: dissolving or dispersing a nucleophilic compound and an amount of an acid additive in a first organic solvent to form a first organic solution or suspension; dissolving an amount of a polymer in a second organic solvent to form a second organic solution; and mixing the first organic solution or suspension and the second solution to form the sustained release formulation, wherein the amount of an acid additive in the sustained release is only a fraction relative to the amount of the polymer and is sufficient to reduce molecular weight reduction of the polymer caused by the nucleophilic compound.
 24. The method of claim 23, wherein the nucleophilic compound is a peptide, ketotifen, thioridazine, risperidone, oxybutynin, olanzapine, naloxone or naltrexone.
 25. The method of claim 23, wherein the acid additive comprises a one more acids having a pKa of 5.0 or lower.
 26. The method of claim 25, wherein the acid additive includes lactic acid, glycolic acid, glacial acetic acid, glyceric acid, benzoic acid, propanoic acid or carboxy terminated oligomers of lactic acid, carboxy terminated oligomers of glycolic acid or a combination of these acids.
 27. The method of claim 23, wherein the first organic solvent is a biocompatible solvent selected from the group consisting of methanol, ethanol, dimethyl sulfoxide (DMSO) and dimethyl acetamide (DMAc).
 28. The method of claim 23, wherein the amount of acid additive in the sustained release is about 2% to about 50% relative to the amount of the polymer.
 29. The method of claim 23, wherein the sustained release is either an emulsion or a homogeneous solution.
 30. The method of claim 23, wherein the polymer is a copolymer of lactic acid and glycolic acid monomers.
 31. A microsphere made by using the sustained release formulation of the method of claim
 30. 32. A sustained release formulation comprising: a biocompatible and biodegradable polymer, wherein the polymer is poly(d,l-lactic acid), poly(l-lactic acid), poly(glycolic acid) or copolymers thereof; at least one nucleophilic substance capable of catalyzing ester bond cleavage and causing molecular weight reduction of the polymer; and an amount of an acid additive such that the polymer in the formulation is less susceptible to molecular weight reduction as compared to the formulation without the acid additive.
 33. The sustained release formulation of claim 2 wherein the polymer is poly(d,l-lactide-co-glycolide) having a molar ratio of lactide to glycolide in the range from 100:0 to 50:50.
 34. The sustained release formulation of claim 1, wherein the nucleophilic substance is a solvent employed in the manufacture of the sustained release formulation.
 35. The sustained release formulation of claim 34 wherein the solvent is propanol, isopropanol, tert-butanol or benzyl alcohol.
 36. A dispersed phase formulation comprising: a biocompatible and biodegradable polymer, wherein the polymer is poly(d,l-lactic acid), poly(l-lactic acid), poly(glycolic acid) or copolymers thereof; at least one nucleophilic ingredient capable of catalyzing ester bond cleavage of the polymer and causing molecular weight reduction of the polymer; and an amount of an acid additive such that the polymer in the formulation is less susceptible to molecular weight reduction as compared to the formulation without the acid additive.
 37. The dispersed phase formulation of claim 15 wherein the polymer is a copolymer of poly-D,L-lactide and poly-D,L-lactide-co-glycolide) having a molar ratio of lactide to glycolide in the range from 100:0 to 50:50.
 38. The dispersed phase formulation of claim 15, wherein the nucleophilic substance is a solvent employed in the manufacture of a sustained release formulation.
 39. The dispersed phase formulation of claim 38 wherein the solvent is propanol, isopropanol, tert-butanol or benzyl alcohol.
 40. The dispersed phase formulation of claim 15, wherein the formulation is further processed to manufacture a sustained release formulation.
 41. A method for preparing a sustained release formulation comprising: forming a mixture comprising a nucleophilic substance, an acid additive, a biocompatible polymer, and a solvent for the polymer; and removing the solvent thereby forming a sustained release formulation wherein the amount of acid additive is such that the polymer in the sustained release formulation is less susceptible to molecular weight reduction as compared to the polymer in the sustained release formulation without the acid additive.
 42. The method of claim 41, wherein the nucleophilic substance is a peptide, ketotifen, thioridazine, olanzapine, risperidone, oxybutynin, naltrexone, octreotide, leuprolide, orntide or Woc4D or pharmaceutically acceptable salts thereof.
 43. The method of claim 41, wherein the acid additive comprises a one more acids having a pKa of 5.0 or lower.
 44. The method of claim 43, wherein the acid additive includes lactic acid, glycolic acid, acetic acid, glyceric acid, benzoic acid, propanoic acid or carboxy terminated oligomers of lactic acid, carboxy terminated oligomers of glycolic acid or a combination of these acids.
 45. The method of claim 41, wherein the amount of acid additive in the sustained release is about 0.1% to about 50% relative to the amount of the polymer.
 46. The method of claim 41, wherein the mixture is an emulsion, a suspension or a homogeneous solution.
 47. The method of claim 41, wherein the polymer is poly(d,l-lactic acid), poly(l-lactic acid), poly(glycolic acid) or copolymers thereof.
 48. The method of claim 41, wherein the polymer is a copolymer of lactic acid and glycolic acid monomers.
 49. The method of claim 41, wherein the polymer is a copolymer of poly-D,L-lactide and poly-D,L-lactide-co-glycolide having a molar ratio of lactide to glycolide in the range from 100:0 to 50:50.
 50. The method of claim 41 wherein the mixture is processed at least at 25° C.
 51. The method of claim 41 wherein the mixture is processed at least at 40° C.
 52. The method of claim 41 wherein the mixture contains a solvent that enhances the reactivity of nucleophilic substances.
 53. The method of claim 41, wherein the solvent for the polymer is selected from the group consisting of methanol, ethanol, propanol, isopropanol, tert-butanol, dichloromethane, and benzyl alcohol.
 54. A microsphere prepared by using the method of claim
 41. 55. A formulation comprising a biodegradable polyester and an amine containing drug wherein the polyester has an acid number of between 10 and
 40. 56. The formulation of claim 55 wherein the polyester composition is at least 50% lactide.
 57. The formulation of claim 55 wherein the amine containing drug is a polypeptide.
 58. The formulation of claim 57 wherein the polypeptide is a GnRH analog, somatostatin analog, hormone, growth factor, or an antibody.
 59. The formulation of claim 55 wherein the formulation further comprises an organic acid.
 60. The formulation of claim 59 wherein the organic acid is an alkyl acid.
 61. The formulation of claim 59 wherein the alkyl acid is acetic acid, lactic acid, glycolic acid, butyric acid, valeric acid, decanoic acid, stearic acid or citric acid.
 62. The formulation of claim 59 wherein the organic acid is an aryl acid.
 63. The formulation of claim 59 wherein the organic acid is present at a level of 0.3% to 8% by weight.
 64. The formulation of claim 55 wherein the acid number is at least 5 wherein the polyester composition is 100% lactide.
 65. The formulation of claim 55 wherein the acid number is at least 15 wherein the polyester composition is 50% lactide and 50% glycolide.
 66. A controlled release formulation, which comprises a matrix of a biocompatible and biodegradable polymer, within which a sufficient amount of polypeptide or a pharmaceutically acceptable salt thereof is uniformly distributed, wherein the biodegradable polymer comprises 100% poly(lactide) or a glycolide containing copolymer comprising at least 75% w/w poly(lactide) wherein the polymer or the copolymer should have an acid number of at least 13 but not greater than 40 and a target load of the polypeptide or the salt thereof is not greater than
 15. 67. The controlled release formulation according to claim 66, wherein the biodegradable polymer is poly-D,L-lactide.
 68. The controlled release formulation according to claim 66, wherein the biodegradable polymer is a blend of poly-D,L-lactide and poly-D,L-lactide-co-glycolide.
 69. The controlled release formulation according to claim 66, wherein the formulation has a target load of the peptide that is less than 15%.
 70. The controlled release formulation according to claim 69, wherein the peptide is selected from the group consisting of octreotide, leuprolide, orntide and Woc4D.
 71. The controlled release formulation according to claim 66, wherein the the formulation further comprises an acid additive.
 72. The controlled release formulation according to claim 71, wherein the acid additive content is about 0.5% to about 5% by weight.
 73. A controlled release formulation, which comprises a matrix of a biocompatible and biodegradable polymer, within which a sufficient amount of polypeptide or a pharmaceutically acceptable salt thereof is uniformly distributed, wherein the biodegradable polymer comprises 100% poly(lactide) having an acid number of at least 5 or a glycolide containing copolymer comprising at least 50% w/w poly(lactide) and having an acid number of at least 13, and wherein the formulation comprises a sufficient amount of an acid additive.
 74. The controlled release formulation according to claim 73, wherein the acid additive is glacial acetic acid, lactic acid, glycolic acid or stearic acid or a combination thereof.
 75. The controlled release formulation according to claim 73, wherein the formulation is either free of hydrophobic peptide related substances or has less than 2% hydrophobic peptide related substances.
 76. A microsphere comprising matrix of a biocompatible and biodegradable polymer, within which a sufficient amount of polypeptide or a pharmaceutically acceptable salt thereof is uniformly distributed, wherein the polymer matrix is made of at least 50% polylactide having an acid number greater than 5 and wherein the polypeptide or the salt thereof has nucleophilic groups that are capable of interacting with acid groups of the polymeric matrix.
 77. The microsphere of claim 76, wherein the polypeptide is present in an amount less than 15 percent by weight relative to the polymer matrix.
 78. The microsphere of claim 76 wherein the polypeptide is selected from the group consisting of octreotide or salts thereof, lanreotide or salts thereof, leuprolide or salts thereof, orntide or salts thereof, a somatostatin analogue and an LHRH antagonist.
 79. The microsphere of claim 76, wherein the polymeric matrix is also made of a co-monomer, glycolide.
 80. A composition for a dispersed phase formulation comprising: (a) a GnRH analog, and (b) an acid additive.
 81. The composition of claim 80, wherein the GnRH analog is an agonist or a freeze-dried antagonist of GnRH.
 82. The composition of claim 81, wherein the GnRH analog is a freeze-dried antagonist of GnRH.
 83. The composition of claim 82, wherein the freeze-dried antagonist of GnRH is lyophilized from a solution comprising a non-aqueous solvent.
 84. The composition of claim 83, wherein said non-aqueous solvent is tert-butyl alcohol or cyclohexane.
 85. The composition of claim 80, wherein the acid additive is an organic or an inorganic acid additive or a combination thereof.
 86. The composition of claim 85, wherein the organic or inorganic acid additive has a pKa of 5.0 or lower.
 87. The composition of claim 86, wherein the organic acid additive is selected from the group consisting of glacial acetic acid, lactic acid, glycolic acid, glyceric acid, benzoic acid, propanoic acid, methane sulfonic acid, mesitylic acid or a combination of these acids.
 88. The composition of claim 86, wherein the inorganic acid additive is HCl.
 89. The composition of claim 80, wherein the composition further comprises a biocompatible and biodegradable polymer.
 90. The dispersed phase formulation of claim 80, wherein the polymer is a poly-D,L-lactide, or a copolymer of D,L-lactide and D,L-glycolide.
 91. A method of increasing the solubility of a high level of a GnRH analogue in a polymer containing dispersed phase, the method comprising: dispensing the high level of the GnRH analogue, wherein the GnRH analogue is an agonist or a freeze dried antagonist of GnRH; adding a first organic solvent to the GnRH analogue to form a first organic mixture; dissolving an amount of a polymer in a second organic solvent to form a second organic mixture; and mixing the first and second organic mixtures to form the dispersed phase, adding an amount of an acid additive to the dispersed phase, wherein the amount of an acid additive in the dispersed phase is sufficient to increase the solubility of the high level of the GnRH analogue in the dispersed phase without affecting the solute release characteristics of any solute bearing microspheres prepared therefrom.
 92. The method of claim 91, wherein the GnRH analogue is the freeze-dried antagonist of GnRH.
 93. The method of claim 92, wherein the freeze-dried antagonist of GnRH is lyophilized from a solution comprising a non-aqueous solvent.
 94. The method of claim 93, wherein said non-aqueous solvent is tert-butyl alcohol or cyclohexane.
 95. The method of claim 92, further comprising heating the dispersed phase to 40 C, or a temperature sufficient to prevent gelling of the dispersed phase.
 96. The method of claim 91, wherein the first organic solvent is methanol, ethanol, dimethyl sulfoxide (DMSO), dimethyl formamide, dimethyl acetamide, N-methylpyrrolidone, dioxane, tetrahydrofuran (THF), methylene chloride, ethylene chloride, carbon tetrachloride, chloroform, diethyl ether, methyl ethyl ether, hexane, cyclohexane, benzene, acetone, ethyl lactate, or ethyl acetate.
 97. A method of increasing solubility of a high level of a freeze-dried antagonist of GnRH in a polymer containing dispersed phase, the method comprising: dissolving the high level of the freeze-dried antagonist of GnRH in a sufficient amount of an acid additive to form a solution; adding an amount of an organic solvent to the solution to form a first organic solution; dissolving an amount of a polymer in an amount of the organic solvent to form a second organic solution; and mixing the first and second organic solutions to form a clear dispersed phase.
 98. The method of claim 97, wherein the method includes an optional step of adding methanol, ethanol, dimethyl sulfoxide (DMSO), dimethyl formamide, dimethyl acetamide, dioxane, tetrahydrofuran (THF), N-methylpyrrolidone, ethylene chloride, carbon tetrachloride, chloroform, diethyl ether, methyl ethyl ether, hexane, cyclohexane, benzene, acetone, ethyl lactate, or ethyl acetate to the solution before the step of adding the organic solvent.
 99. The method of claim 97, wherein the organic solvent is dichloromethane.
 100. The method of claim 97, wherein the acid additive is an organic acid or an inorganic acid or a combination thereof.
 101. The method of claim 97, wherein the acid additive has a pKa of 5.0 or lower.
 102. The method of claim 101, wherein the acid additive is glacial acetic acid, lactic acid, glycolic acid, glyceric acid, benzoic acid, propanoic acid, methane sulfonic acid, mesitylic acid or HCl or a combination of these acids.
 103. A solute containing microsphere prepared from the dispersed phase of the method of claim 97, via removal of the organic solvent, the acid additive, and any other organic liquid present in the dispersed phase.
 104. The solute containing microsphere of claim 103, wherein the solute in the microsphere is a GnRH analog.
 105. The solute containing microsphere of claim 104, wherein the GnRH analog is an antagonist.
 106. The solute containing microsphere of claim 104, wherein the GnRH analog is an antagonist.
 107. A method for suppressing a gonadotropin releasing hormone in a mammal suffering from said hormone related disorder comprising administering an effective amount of a composition comprising the solute containing microsphere of claim 104 to the mammal.
 108. The method of claim 107, wherein said disorder is a testosterone dependent disorder, benign prostate hypertrophy or prostate cancer.
 109. The method of claim 108, wherein said composition is administered subcutaneously or intramuscularly.
 110. The method of claim 107 wherein said mammal is a human. 